ウルトラミクロトームにおけるnanosectioning過程での重合体破壊と変形【Powered by NICT】

Polymer fracture and deformation during nanosectioning in an ultramicrotome

著者 (5件)： Sun Fengzhen (Division of Applied Mechanics, Department of Engineering Sciences, Uppsala University, SE-751 21, Sweden) ,  Li Hu (Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, SE-751 21, Sweden) ,  Lindberg Henrik (Division of Applied Mechanics, Department of Engineering Sciences, Uppsala University, SE-751 21, Sweden) ,  Leifer Klaus (Division of Applied Materials Science, Department of Engineering Sciences, Uppsala University, SE-751 21, Sweden) ,  Gamstedt E. Kristofer (Division of Applied Mechanics, Department of Engineering Sciences, Uppsala University, SE-751 21, Sweden)
資料名： Engineering Fracture Mechanics  (Engineering Fracture Mechanics)
巻： 182  ページ： 595-606  発行年： 2017年 
JST資料番号： A0119A  ISSN： 0013-7944  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： nanosectioningプロセスにおける熱可塑性プラスチックの破壊と変形挙動を力変換器を用いたウルトラミクロトーム計装を用いて研究した。10~100nmのための厚さ値と断面については,ポリメタクリル酸メチルの表面形成の特異的研究は,共有結合を破壊する6.3Jm~ 2であり,巨視的破壊靭性にかなり小さいが,1.5Jm~ 2の理論的比表面エネルギーに相対的に近いことが分かった。切片表面上の百nm間隔,周期的横方向特徴は臨界厚さ以上の断面の原子間力顕微鏡で観察した。変形モードの遷移は,ある厚さ,断熱剪断帯を示す他の材料の切断実験と協調してで起こることを明らかにした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 破壊靱性 ,  変換器 ,  表面エネルギー ,  *重合体 ,  ポリメタクリル酸メチル ,  原子間力顕微鏡 ,  熱可塑性プラスチック ,  共有結合
準シソーラス用語： 断熱剪断帯 ,  変形モード ,  変形挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： Nanosectioning ,  破壊 ,  局部変形 ,  周期的特徴 ,  断熱せん断