アルカリ溶液中でのバインダレスWC材料とWC-Co超硬合金の腐食と強度劣化挙動:比較研究【Powered by NICT】

Corrosion and strength degradation behaviors of binderless WC material and WC-Co hardmetal in alkaline solution: A comparative investigation

著者 (5件)： Tang Wei (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Zhang Li (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Chen Yi (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Zhang Huadong (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China) ,  Zhou Lei (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China)
資料名： International Journal of Refractory Metals & Hard Materials  (International Journal of Refractory Metals & Hard Materials)
巻： 68  ページ： 1-8  発行年： 2017年 
JST資料番号： H0059B  ISSN： 0263-4368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 不十分な耐食性はWC-Co超硬合金の主な弱点であり,従って,バインダレスWC材料(bWCs)は,このような厳しい使用条件における有望な代替として考えられている。それにもかかわらず,腐食抵抗の定量的差と二種の材料の腐食による強度劣化の知識は限られている。良好に緻密化した直線bWCとWC-10Co超硬合金をスパークプラズマ焼結と焼結H IPにより作製した。重量損失,溶液分析によって行い,走査電子顕微鏡,X線光電子分光法ならびにX線回折計により支援された腐食研究は一貫してbWCは1M NaOH溶液中で優れた耐食性を示すことを示した。28日の期間における重量損失により評価したWC-10Coの平均腐食速度(0.045mm/y)はbWCのそれの約6.4倍であった。,すなわち,二つの材料の間の強度ギャップそれらの元の状態で4.4倍から連続的に28日間浸漬後2倍ににおける実質的な強度低下と狭小化を観察した。関連腐食挙動を検討した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *超硬合金 ,  浸漬 ,  焼結 ,  X線回折計 ,  耐食性 ,  重量損失 ,  *腐食 ,  緻密化 ,  走査電子顕微鏡 ,  腐食速度 ,  放電プラズマ焼結 ,  X線光電子分光法
準シソーラス用語： 腐食挙動 ,  *バインダレス ,  *アルカリ溶液 , 【Automatic Indexing@JST】

著者キーワード (6件)： バインダレスWC材料 ,  超硬 ,  浸漬 ,  腐食速度 ,  強度劣化 ,  相乗腐食