ゲル高分子電解質調製と色素増感太陽電池応用のためのポリプロピレンカーボネート高分子に関する調査【Powered by NICT】

Exploration on polypropylene carbonate polymer for gel polymer electrolyte preparation and dye-sensitized solar cell application

著者 (4件)： Farhana N. K. (Department of Physics, Faculty of Science, Center for Ionics University of Malaya, University of Malaya, Kuala Lumpur, 50603, Malaysia) ,  Khanmirzaei Mohammad H. (Department of Physics, Faculty of Science, Center for Ionics University of Malaya, University of Malaya, Kuala Lumpur, 50603, Malaysia) ,  Ramesh S. (Department of Physics, Faculty of Science, Center for Ionics University of Malaya, University of Malaya, Kuala Lumpur, 50603, Malaysia) ,  Ramesh K. (Department of Physics, Faculty of Science, Center for Ionics University of Malaya, University of Malaya, Kuala Lumpur, 50603, Malaysia)
資料名： Journal of Applied Polymer Science  (Journal of Applied Polymer Science)
巻： 134  号： 29  ページ： ROMBUNNO.45091  発行年： 2017年 
JST資料番号： C0467A  ISSN： 0021-8995  CODEN： JAPNAB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： ポリプロピレンカーボネート(PPC)ポリマの導入とよう化ナトリウム(NaI)塩の異なる重量パーセントを含むゲル高分子電解質(GPE)を調製した。エチレンカルボナートとプロピレンカルボナートを可塑剤として使用されている。2.01mS cm~ 1の最大イオン伝導率は室温で達成した。温度依存イオン伝導率研究を行った。GPEはFourier変換赤外(FTIR)を用いて構造特性を調べた。FTIR分析は,PPCとNaIの間の錯体生成が起こっていることを確認した。GPEを用いて,色素増感太陽電池(DSSC)は太陽光強度下で作製した。6.38%の最高のエネルギー変換効率は60wt%NaIの取り込みを達成した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 錯体生成 ,  *ゲル ,  温度依存性 ,  ヨウ化ナトリウム ,  Fourier変換 ,  エネルギー変換効率 ,  可塑剤 ,  構造特性 ,  *高分子
準シソーラス用語： 太陽光強度 ,  イオン伝導率 ,  *ポリプロピレンカーボネート ,  *色素増感太陽電池 ,  *ゲル電解質 , 【Automatic Indexing@JST】

著者キーワード (3件)： 応用 ,  電気化学 ,  ゲル

分類 (2件)： 高分子固体の物理的性質  (CG02024U) ,  その他の高分子材料  (YH07150C)

タイトルに関連する用語 (7件)： ゲル高分子電解質 ,  調製 ,  色素増感太陽電池 ,  応用 ,  ポリプロピレンカーボネート ,  高分子 ,  調査