活性スクリーンプラズマ窒化処理した420マルテンサイト系ステンレス鋼の摩耗と腐食特性【Powered by NICT】

Wear and corrosion properties of AISI 420 martensitic stainless steel treated by active screen plasma nitriding

著者 (7件)： Li Yang (State Key Laboratory of Tribology, Tsinghua University, Beijing, 100084, PR China) ,  Li Yang (Department of Materials Science and Engineering, Yantai University, Yantai, 264005, PR China) ,  He Yongyong (State Key Laboratory of Tribology, Tsinghua University, Beijing, 100084, PR China) ,  Xiu JunJie (Department of Materials Science and Engineering, Yantai University, Yantai, 264005, PR China) ,  Wang Wei (State Key Laboratory of Tribology, Tsinghua University, Beijing, 100084, PR China) ,  Zhu YiJie (Department of Materials Science and Engineering, Yantai University, Yantai, 264005, PR China) ,  Hu Baoguo (State Key Laboratory of Tribology, Tsinghua University, Beijing, 100084, PR China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 329  ページ： 184-192  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 420マルテンサイトステンレス鋼を活性スクリーンプラズマ窒化によって処理した。試験表を鋼スクリーン内に置かれたが,陰極電位から単離した。炉壁と検査表と共に,試料は接地した,アノード電位が形成された。処理は440~520°Cの温度範囲で6時間,400PaのNH_3雰囲気中で行った。試料を走査電子顕微鏡(SEM),原子間力顕微鏡(A FM),X線光電子分光法(XPS),X線回折(XRD)および微小硬さ測定によって特性化した。結果は陽極窒化処理して,種々の温度で異なるタイプの改質表面層を生成できることを示した。窒化層と表面粗さの厚さは窒化温度と共に増加した。乾燥滑り摩耗試験と電気化学的腐食試験は,未処理基板と窒化した試験片について実施した。アノード電位でアクティブスクリーンプラズマ窒化は420ステンレス鋼の硬度,耐摩耗性および腐食特性を改善することを結論できる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： X線光電子分光法 ,  耐摩耗性 ,  *スクリーン ,  電気化学的腐食試験 ,  X線回折 ,  *摩耗 ,  表層 ,  走査電子顕微鏡 ,  *イオン窒化 ,  *ステンレス鋼 ,  微小硬さ ,  電位 ,  窒化層 ,  原子間力顕微鏡
準シソーラス用語： *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： プラズマ窒化 ,  420ステンレス鋼 ,  摩耗 ,  孔食

分類 (1件)： 表面硬化熱処理  (WC03030E)

タイトルに関連する用語 (6件)： 活性 ,  スクリーン ,  プラズマ窒化 ,  マルテンサイト系ステンレス鋼 ,  摩耗 ,  腐食特性