Brillouin腐食膨張センサに基づいたコンクリートの損傷評価【Powered by NICT】

Damage evaluation of concrete based on Brillouin corrosion expansion sensor

著者 (4件)： Lv Haifeng (School of Civil Engineering, State Key Laboratory of Coastal and Offshore Engineering, Dalian University of Technology, Dalian, Liaoning 116024, China) ,  Zhao Xuefeng (School of Civil Engineering, State Key Laboratory of Coastal and Offshore Engineering, Dalian University of Technology, Dalian, Liaoning 116024, China) ,  Zhan Yilin (School of Civil Engineering, State Key Laboratory of Coastal and Offshore Engineering, Dalian University of Technology, Dalian, Liaoning 116024, China) ,  Gong Peng (School of Civil Engineering, State Key Laboratory of Coastal and Offshore Engineering, Dalian University of Technology, Dalian, Liaoning 116024, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 143  ページ： 387-394  発行年： 2017年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 鉄筋腐食による鉄筋コンクリートの損傷度を評価するために,損傷因子は初期亀裂前および亀裂の発生の間のコンクリートの損傷度を定量的に評価するために提案した。Brillouin光ファイバ時間領域解析(BOTDA)センサを作製した鋼の腐食膨張歪を監視した。腐食センサを埋め込んだ二コンクリート試験片が作成された。鋼腐食過程を加速するために加速腐食実験プログラム。実験結果は,腐食センサは鋼の腐食膨張歪を実時間で監視できることを示した。最後に,損傷因子によるモニタリング結果をマッピングするために,有限要素分析は,界面コンクリートとコンクリートカバーのクラックひずみを決定するために鋼の腐食のプロセスをシミュレートするために使用される。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 亀裂 ,  *腐食 ,  鋼 ,  光ファイバ ,  *センサ ,  鉄筋コンクリート ,  界面 ,  *コンクリート
準シソーラス用語： 有限要素解析 ,  腐食センサ ,  膨張ひずみ ,  時間領域解析 ,  損傷度 ,  鉄筋腐食 ,  *損傷評価 , 【Automatic Indexing@JST】

著者キーワード (5件)： 腐食 ,  BOTDA ,  損傷因子 ,  クラッキング ,  有限要素(FE)

分類 (1件)： コンクリート構造  (RA04030A)

タイトルに関連する用語 (4件)： 腐食 ,  膨張 ,  コンクリート ,  損傷評価