天然源からのハロイサイトカルボキシメチルセルロースクリオゲル複合材料【Powered by NICT】

Halloysite-carboxymethyl cellulose cryogel composite from natural sources

著者 (4件)： Sengel Sultan Butun (Canakkale Onsekiz Mart University, Faculty of Sciences and Arts, Chemistry Department, Nanoscience and Technology Research and Application Center (NANORAC), Terzioglu Campus, 17100 Canakkale, Turkey) ,  Sahiner Mehtap (Ege University, Engineering Faculty, Leather Engineering Department, Bornova, 35100 Izmir, Turkey) ,  Aktas Nahit (Yuzuncu Yil University, Chemical Engineering Faculty, Chemical Engineering Department, 65080 Van, Turkey) ,  Sahiner Nurettin (Canakkale Onsekiz Mart University, Faculty of Sciences and Arts, Chemistry Department, Nanoscience and Technology Research and Application Center (NANORAC), Terzioglu Campus, 17100 Canakkale, Turkey)
資料名： Applied Clay Science  (Applied Clay Science)
巻： 140  ページ： 66-74  発行年： 2017年 
JST資料番号： B0687B  ISSN： 0169-1317  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,カルボキシメチルセルロース(CMC)とハロイサイトナノチューブ(Halナノチューブ)のような天然源を用いた新しい超多孔性複合体クリオゲルを調製した。複合材料は低温ゲル化前に高分子マトリックス内のHalナノチューブを含む低温ゲル化法により調製した。一連Halナノチューブ/カルボキシメチルセルロース複合材料の架橋剤,Halナノチューブ量の使用量を変化させて調製した。,Halナノチューブは(3-アミノプロピル)トリエトキシシラン(APTES), (3-クロロ-2-ヒドロキシプロピル)トリメチルアンモニウムクロリド(CHPTACI),ポリエチレンイミン(PEI),エピクロロヒドリン(ECH),ジエチレントリアミン(DETA),タウリン(TA),とトリス(2 アミノエチル)アミン(TAEA)のような異なる改質剤で修飾した,これらの修飾HalナノチューブはCMCクリオゲル複合材料調製に使用した。合成した材料のキャラクタリゼーションを走査および透過電子顕微鏡(SEMおよびTEM),ゼータ電位(ZP)測定,熱重量分析(TGA),Fourier変換赤外(FT IR)分光測定,表面積と多孔性分析器により行った。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： Fourier変換 ,  ゲル化 ,  透過型電子顕微鏡 ,  表面積 ,  ナノチューブ ,  ζ電位 ,  *複合材料 ,  熱重量分析 ,  低温 ,  キャラクタリゼーション ,  多孔性
準シソーラス用語： 材料調製 ,  *クリオゲル , 【Automatic Indexing@JST】

著者キーワード (5件)： ハロイサイトナノチューブ ,  カルボキシメチルセルロースクリオゲル/ヒドロゲル ,  超多孔質 ,  粘土複合材料クリオゲル/ヒドロゲル ,  化学修飾