Zn-assisted magnesiothermic reduction for the preparation of ultra-fine silicon nanocrystals for lithium ion batteries

著者 (8件)： Ren Yongpeng (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Zhou Xiangyang (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Zhou Haochen (School of Aerospace Engineering, Tsinghua University, Beijing 100083, PR China) ,  Yang Juan (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Chen Song (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Wu Lili (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Nie Yang (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China) ,  Wang Biao (School of Metallurgy and Environment, Central South University, Changsha 410083, PR China)
資料名： Chemical Engineering Journal  (Chemical Engineering Journal)
巻： 328  ページ： 691-696  発行年： 2017年 
JST資料番号： D0723A  ISSN： 1385-8947  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Siアノード材料を得るための亜鉛-ケイ素合金dealloyとマグネシウム熱還元プロセスを融合した。亜鉛支援マグネシウム熱還元により,得られたSiは,均一なメソ多孔質構造,大きな表面積,高い細孔容積および良く分散したSi結晶粒,Zn遊離のものと非常に異なるを有していた。作製したままのSiアノードは,高い可逆容量と良好なサイクル安定性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ケイ素 ,  表面積 ,  *リチウムイオン電池 ,  合金 ,  *亜鉛 ,  ケイ素合金 ,  結晶粒
準シソーラス用語： 可逆容量 ,  細孔容積 ,  メソポーラス ,  アノード材料【電池】 ,  *マグネシウム熱還元 , 【Automatic Indexing@JST】

著者キーワード (5件)： 多孔質シリコン ,  マグネシウム熱還元 ,  リチウムイオン電池アノード ,  シリコンナノロッド ,  合金

分類 (2件)： 触媒操作  (XE01050T) ,  電極過程  (CB07040U)

タイトルに関連する用語 (7件)： リチウムイオン電池 ,  超微細 ,  シリコンナノ結晶 ,  調製 ,  Zn ,  支援 ,  マグネシウム熱還元