防汚特性のためのゾル-ゲル法によるアルミナ膜の表面改質【Powered by NICT】

Surface modification of alumina membranes via a sol-gel process for antifouling properties

著者 (5件)： Wang Fei (Powder and Ceramics Division, Korea Institute of Materials Science (KIMS), 797 Changwondaero, Seongsangu, Changwon 51508, Republic of Korea) ,  Wang Fei (Key Laboratory of Tropical Crop Products Processing of Ministry of Agriculture, Agricultural Products Processing Research Institute, Chinese Academy of Tropical Agricultural Sciences, Zhanjiang 524001, China) ,  Lee Jongman (Powder and Ceramics Division, Korea Institute of Materials Science (KIMS), 797 Changwondaero, Seongsangu, Changwon 51508, Republic of Korea) ,  Ha Jang-Hoon (Powder and Ceramics Division, Korea Institute of Materials Science (KIMS), 797 Changwondaero, Seongsangu, Changwon 51508, Republic of Korea) ,  Song In-Hyuck (Powder and Ceramics Division, Korea Institute of Materials Science (KIMS), 797 Changwondaero, Seongsangu, Changwon 51508, Republic of Korea)
資料名： Materials Letters  (Materials Letters)
巻： 191  ページ： 200-202  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： アルミナ膜は膜ファウリングを緩和するSiO_2ゾル-ゲルプロセスを用いて修飾した。SiO_2被覆層の形成はわずかに狭くなった細孔径をもたらし,純水透過率を減少させた。低等電点のために,SiO_2~被覆膜は強い負の表面電荷(pH=6.5で 130mV),フミン酸に対する静電反発力の存在に帰着した。より高いTEOS(オルトケイ酸テトラエチル)濃度を持つ膜は膜ファウリング過程で高いフラックスレベルを示したが,元の状態のアルミナ膜は最も低い流束をdisplaid。非晶質SiO_2無機表面改質を,元の状態のアルミナ膜の防汚特性が明らかに向上する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 被覆層 ,  *ゲル ,  等電点 ,  *アルミナ ,  斥力 ,  細孔径 ,  皮膜 ,  *表面改質 ,  純水 ,  表面電荷 ,  透過率 ,  *ゾル-ゲル法 ,  フミン酸
準シソーラス用語： オルトケイ酸 ,  膜ファウリング , 【Automatic Indexing@JST】

著者キーワード (4件)： セラミックス ,  ゾル-ゲル調製 ,  表面改質 ,  防汚

分類 (1件)： 酸化物薄膜  (BK14050P)

タイトルに関連する用語 (4件)： 防汚 ,  ゾル-ゲル法 ,  アルミナ膜 ,  表面改質