ナノ結晶Mg_24Y_3Ni GR複合材料の微細構造と水素貯蔵特性に及ぼす黒鉛(GR)含有量の影響【Powered by NICT】

Effect of graphite (GR) content on microstructure and hydrogen storage properties of nanocrystalline Mg₂₄Y₃-Ni-GR composites

著者 (15件)： Yang Tai (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin 300130, China) ,  Yang Tai (Tianjin Key Laboratory of Laminating Fabrication and Interface Control Technology for Advanced Materials, Hebei University of Technology, Tianjin 300130, China) ,  Yang Tai (Department of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081, China) ,  Liang Chunyong (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin 300130, China) ,  Liang Chunyong (Tianjin Key Laboratory of Laminating Fabrication and Interface Control Technology for Advanced Materials, Hebei University of Technology, Tianjin 300130, China) ,  Wang Xinghua (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin 300130, China) ,  Wang Xinghua (Tianjin Key Laboratory of Laminating Fabrication and Interface Control Technology for Advanced Materials, Hebei University of Technology, Tianjin 300130, China) ,  Wang Hongshui (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin 300130, China) ,  Wang Hongshui (Tianjin Key Laboratory of Laminating Fabrication and Interface Control Technology for Advanced Materials, Hebei University of Technology, Tianjin 300130, China) ,  Yuan Zeming (Department of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081, China) ,  Yin Fuxing (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin 300130, China) ,  Yin Fuxing (Tianjin Key Laboratory of Laminating Fabrication and Interface Control Technology for Advanced Materials, Hebei University of Technology, Tianjin 300130, China) ,  Li Qiang (Research Institute for Energy Equipment Materials, Hebei University of Technology, Tianjin 300130, China) ,  Li Qiang (Tianjin Key Laboratory of Laminating Fabrication and Interface Control Technology for Advanced Materials, Hebei University of Technology, Tianjin 300130, China) ,  Zhang Yanghuan (Department of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 726  ページ： 498-506  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 三元Mg_24Y_3 5wt.%Ni-x wt.%GR(x=0 10)複合材料を機械的ボールミル粉砕によって調製した。相組成,微細構造と水素貯蔵特性をX線粉末回折(XRD),走査電子顕微鏡(SEM),透過型電子顕微鏡(TEM),およびSievert試験法により特性化した。結果はGRの適切な量を添加粒子サイズを減少させるとボールミル粉砕効率の促進に有益な影響を及ぼすことを示した。3wt.%GR含量の試料は100°Cでも,結果として,非晶質およびナノ結晶優れた水素吸収動力学を示すから成る複合構造を有する示差走査熱量測定(DSC)試験を用いて,脱水素性能を評価した。ピーク温度はGR含量を0から0~3wt.%の325°Cから295°Cに低下し,それは触媒NiとMg_24Y_3合金粒子間の結晶粒微細化と接触改善に起因すると考えられる。しかし,より大きなフレーク状Mg_24Y_3合金粒子はGR含量のさらなる増加,主に過剰GR添加ボールミル効率を低下させるに起因すると観察された。利点は10wt.%までのGR添加量と完全に消失したであろう。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *微細構造 ,  相組成 ,  ボールミル ,  透過型電子顕微鏡 ,  *水素吸蔵 ,  X線回折 ,  *ナノ結晶 ,  *グラファイト ,  *複合材料 ,  *ニッケル ,  示差走査熱量測定 ,  走査電子顕微鏡
準シソーラス用語： 金粒子 ,  粉末X線回折 ,  ボールミル摩砕 , 【Automatic Indexing@JST】

著者キーワード (5件)： 水素貯蔵 ,  Mg基合金 ,  ナノ結晶 ,  Catalysis ,  Kinetics

分類 (1件)： その他の金属組織学  (WB01040Y)