文献

J-GLOBAL ID：201702226727003219   整理番号：17A1703164

対電極としてのMoO_3を用いた太陽電池応用のための硫化鉛増感ZrO_2光アノード【Powered by NICT】

Lead sulphide sensitized ZrO₂ photoanode for solar cell application with MoO₃ as a counter electrode

著者 (6件)： Bhalekar Vikram P. (Advanced Physics Laboratory, Department of Physics, Savitribai Phule Pune University, Pune 411007, India) ,  Baviskar Prashant K. (Advanced Physics Laboratory, Department of Physics, Savitribai Phule Pune University, Pune 411007, India) ,  Prasad Bikram (Advanced Physics Laboratory, Department of Physics, Savitribai Phule Pune University, Pune 411007, India) ,  Beedri Niyamat I. (Advanced Physics Laboratory, Department of Physics, Savitribai Phule Pune University, Pune 411007, India) ,  Kadam Vishal S. (Advanced Physics Laboratory, Department of Physics, Savitribai Phule Pune University, Pune 411007, India) ,  Pathan Habib M. (Advanced Physics Laboratory, Department of Physics, Savitribai Phule Pune University, Pune 411007, India)
資料名： Chemical Physics Letters  (Chemical Physics Letters)
巻： 689  ページ： 15-18  発行年： 2017年 
JST資料番号： B0824A  ISSN： 0009-2614  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 室温連続イオン層吸着と反応技術を,素子級応用のためのZrO_2上のPbSを増感する効率的に使用した。本研究で用いた化学的アプローチは開発コストを低減させる。PbS増感ZrO_2の紫外-可視研究は可視領域で良好な光学被覆を示した。最後に,デバイス作製は,電解質とMoO_3対電極として光アノード,多硫化物としてPbS増感ZrO_2を行った。PbS上の表面不動態化(ZnS)の影響も調べた。表面不動態化ZrO_2/PbS装置であるZrO_2/PbS(0.55%)より~3倍高い1.53%の効率の改善を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *硫化鉛 ,  *増感 ,  *太陽電池 ,  電解質 ,  多硫化物 ,  吸着 ,  硫化亜鉛
準シソーラス用語： 表面不動態化 ,  光学被覆 ,  可視領域 ,  *光アノード ,  *対極 , 【Automatic Indexing@JST】

著者キーワード (7件)： ZrO_2 ,  PbS ,  表面不動態化 ,  化学経路 ,  MoO_3 ,  EIS ,  太陽電池

分類 (2件)： 太陽電池  (NC03084O) ,  電気化学反応  (CB07050F)

タイトルに関連する用語 (5件)： 対電極 ,  太陽電池 ,  応用 ,  硫化鉛 ,  光アノード