Vertically Oriented 2D Layered Perovskite Solar Cells with Enhanced Efficiency and Good Stability

著者 (11件)： Zhang Xinqian (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Zhang Xinqian (Department of Chemical Engineering, Xinjiang Agriculture University, Urumqi, 830052, P. R. China) ,  Wu Gang (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Yang Shida (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Fu Weifei (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Zhang Zhongqiang (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Chen Chen (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Liu Wenqing (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Yan Jielin (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Yang Weitao (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China) ,  Chen Hongzheng (State Key Laboratory of Silicon Materials, MOE Key Laboratory of Macromolecular Synthesis and Functionalization, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou, 310027, P. R. China)
資料名： Small  (Small)
巻： 13  号： 33  ページ： ROMBUNNO.201700611  発行年： 2017年 
JST資料番号： W2348A  ISSN： 1613-6810  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 垂直配向した高結晶性2D層状(BA)2(MA)n_ 1Pb_nI_3_n_+1(BA=CH_3(CH_2)3NH_3,MA=CH_3NH_3,n=3 4)ペロブスカイト薄膜を一段階スピンコーティングプロセスによる添加剤チオシアン酸アンモニウム(NH_4SCN)を用いて作製した。湿潤雰囲気(H_r=55±5%)に曝露された40日間後の膜の湿度安定性はほとんど変化しないX線回折パターンによって保証された。インジウムすず酸化物(ITO)/ポリ(3,4-エチレンジオキシチオフェン):ポリ(スチレン-スルホナート)/(BA)2(MA)n_ 1Pb_nI_3_n_+1(n=3,4)/[6,6]-フェニルC_61酪酸メチルester/Bathocuproine/Agの構造と光起電素子を作製した。BAI:メチルアンモニウムよう化物:PbI_2:NH_4SCN=2:2:3:1の前駆体組成(モル比)(BA)2(MA)2Pb_3I_10ペロブスカイト(n=3)に基づく素子は6.82%の平均電力変換効率(PCE)を示した。(BA)2(MA)3Pb_4I_13(n=4)の場合,8.79%の高いPCEを達成した。非密封デバイスの両方は,精製N_2グローブボックス中で貯蔵期間中に殆ど変化しなかったPCEを持つユニークな安定性を行った。本研究では,2dペロブスカイト太陽電池の効率を高めるための簡単で効果的な方法を提供する。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *太陽電池 ,  ヨウ化物 ,  グローブボックス ,  湿度 ,  前駆体 ,  添加剤 ,  *効率化 ,  シェルフライフ ,  X線回折 ,  *二次元 ,  結晶度 ,  湿潤
準シソーラス用語： 電力変換効率 ,  チオシアン酸アンモニウム ,  *垂直配向 , 【Automatic Indexing@JST】