CFRP/Mg積層板のモードIおよびモードII層間強度に及ぼす表面前処理の影響【Powered by NICT】

Effects of surface pre-treatments on Mode I and Mode II interlaminar strength of CFRP/Mg laminates

著者 (6件)： Pan Yingcai (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Wu Guoqing (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Huang Zheng (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Li Maoyuan (The System Design Institute of Mechanical-Electrical Engineering Beijing, Beijing 100048, China) ,  Ji Sudong (The System Design Institute of Mechanical-Electrical Engineering Beijing, Beijing 100048, China) ,  Zhang Zongke (School of Materials Science and Engineering, Beihang University, Beijing 100191, China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 319  ページ： 309-317  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,三つの異なる表面改質技術,グリットブラスト,マイクロアーク酸化(MAO)とレーザアブレーションをそれぞれマグネシウム合金シートにおいて実行し,処理された表面は,表面トポグラフィーと表面粗さ特性を評価した。に加えて,層間強度とCFRP/Mg積層板の界面破壊特性を調べた,モードI(剥離)とモードII(せん断)荷重を受けるCFRP/Mg積層板の層間強度と破壊機構に及ぼす種々の前処理技術の効果を包括的に解析した。結果は,グリットブラスト表面と比較して,MAO処理は,せん断強さのわずかな増加をもたらすことを示した,それは弱いMAO coating/Mg基板界面のために最悪の剥離強度結果を与える。レーザアブレーションは,剥離およびせん断荷重を受けるCFRP/Mg積層材の全体的な層間強度を効果的に増強する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： マグネシウム合金 ,  表面改質 ,  剪断荷重 ,  *炭素繊維強化プラスチック ,  剪断強さ ,  積層材料 ,  *積層板 ,  界面 ,  剪断 ,  *前処理 ,  レーザアブレーション ,  破壊機構 ,  界面破壊 ,  グリットブラスト ,  剥離強度 ,  機械的性質 ,  強度
準シソーラス用語： 剥離強さ , 【Automatic Indexing@JST】

著者キーワード (6件)： 繊維金属積層材料 ,  マグネシウム合金 ,  マイクロアーク酸化 ,  レーザアブレーション ,  剥離強度 ,  せん断強度

分類 (4件)： その他の表面処理  (WC08070F) ,  医用素材  (GA05040H) ,  表面処理  (YH04112X) ,  金属への塗装  (YJ04030I)

タイトルに関連する用語 (4件)： CFRP ,  Mg ,  積層板 ,  前処理