鋼ストランドの付着寿命劣化と複合腐食と疲労を受けるコンクリート【Powered by NICT】

Bond life degradation of steel strand and concrete under combined corrosion and fatigue

著者 (5件)： Li Fumin (Jiangsu Key Laboratory of Environmental Impact and Structural Safety in Engineering, China University of Mining and Technology, Xuzhou, Jiangsu, China) ,  Li Fumin (State Key Laboratory for Geomechanics and Deep Underground Engineering, China University of Mining and Technology, Xuzhou, Jiangsu, China) ,  Qu Yaxu (Jiangsu Key Laboratory of Environmental Impact and Structural Safety in Engineering, China University of Mining and Technology, Xuzhou, Jiangsu, China) ,  Qu Yaxu (China Machinery TDI International Engineering Co., ltd, Luoyang, Henan, China) ,  Wang Jianghao (Jiangsu Key Laboratory of Environmental Impact and Structural Safety in Engineering, China University of Mining and Technology, Xuzhou, Jiangsu, China)
資料名： Engineering Failure Analysis  (Engineering Failure Analysis)
巻： 80  ページ： 186-196  発行年： 2017年 
JST資料番号： W0684A  ISSN： 1350-6307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 腐食疲労損傷によって誘起された鋼棒とコンクリートの間の結合の破壊は,コンクリート構造研究において重要であるが,関連した研究は少ない。プレテンショニングプレストレストコンクリート構造物における結合の腐食疲れ損傷挙動を研究することを目的とした。鋼ストランドとコンクリートの20種の接着試験片のための慢性腐食と疲労(即ち,三レベルの腐食と八レベル疲労)の複合作用を行った。結果は結合の腐食疲労破壊は主に分割モードで起こることを示した。結合の腐食-疲労寿命は腐食の一定作用下で増加した疲れ応力範囲で減少した。同様に,結合の腐食-疲労寿命は一定疲労作用下で増加し腐食電流密度とともに減少した。腐食疲れ結合寿命の経験的モデルは実験結果を回帰および拡張することにより確立した。モデルから,二百万の一定寿命の腐食と疲労の相関式を導出した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *付着 ,  疲れ寿命 ,  棒鋼 ,  接着試験 ,  *腐食 ,  腐食電流 ,  コンクリート構造 ,  *鋼 ,  *コンクリート ,  プレテンショニング ,  *ストランド ,  腐食疲れ
準シソーラス用語： 経験モデル ,  複合作用 ,  プレストレストコンクリート構造物 , 【Automatic Indexing@JST】

著者キーワード (5件)： プレストレストコンクリート構造物 ,  Strand ,  結合 ,  腐食疲れ ,  寿命

分類 (1件)： コンクリート構造  (RA04030A)

タイトルに関連する用語 (6件)： 鋼 ,  ストランド ,  寿命 ,  腐食 ,  疲労 ,  コンクリート