J-GLOBAL ID：201702229298348248   整理番号：17A0448647

室温でのCOへの高応答を示す棒状Au/In-2O_3ナノ複合材料の容易な調製【Powered by NICT】

Facile preparation of rod-like Au/In₂O₃ nanocomposites exhibiting high response to CO at room temperature

著者 (5件)： Fu Huifen (State Key Laboratory of Chemical Resource, Beijing University of Chemical Technology, Beijing 100029, China) ,  Hou Changliang (State Key Laboratory of Chemical Resource, Beijing University of Chemical Technology, Beijing 100029, China) ,  Gu Fubo (State Key Laboratory of Chemical Resource, Beijing University of Chemical Technology, Beijing 100029, China) ,  Han Dongmei (State Key Laboratory of Chemical Resource, Beijing University of Chemical Technology, Beijing 100029, China) ,  Wang Zhihua (State Key Laboratory of Chemical Resource, Beijing University of Chemical Technology, Beijing 100029, China)
資料名： Sensors and Actuators. B. Chemical  (Sensors and Actuators. B. Chemical)
巻： 243  ページ： 516-524  発行年： 2017年 
JST資料番号： T0967A  ISSN： 0925-4005  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 棒状In_2O_3ナノ材料はIn源としてIn(NO_3)3を用いて100°Cで大気圧下で調製した。調製過程中にHNTAはアルカリ環境を提供し,ロッド状構造の形成に導く構造誘導剤として作用させた。棒状Au/In_2O_3はNaBH_4によるHAuCl_4のin situ還元により生成した。純In_2O_3は室温(25°C)でのCOへの応答を示さなかった。Au In_2O_3の負荷は非常に豊富な表面吸着酸素種によるガス検知性能を改善した。低動作温度は応答の改善に有利であった。高アニーリング温度はロッド状構造の破壊とAuの成長をもたらし,応答の減少をもたらした。300°Cでアニールした棒状Au/In_2O_3が最良の性能を示した。100ppm COに対する応答は約9であり,応答時間と回復時間は全て約30sであった。安定性及び選択性は良好であった。電子空乏層原理は棒状In_2O_3とAu/In_2O_3に対する応答の相違を説明するために用いた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 酸素 ,  *ナノ複合材料 ,  空乏層 ,  *金 ,  ナノ材料 ,  応答時間
準シソーラス用語： 回復時間 ,  アニーリング温度 ,  動作温度 ,  ガス検知 ,  表面吸着 ,  構造誘導剤 , 【Automatic Indexing@JST】

著者キーワード (4件)： 棒状Au/Inは_2O_3 ,  Nanomaterial ,  COガスセンサ ,  室温

分類 (1件)： 分析機器  (CC02020S)

タイトルに関連する用語 (6件)： 室温 ,  CO ,  応答 ,  Au ,  ナノ複合材料 ,  調製