冷却結晶棒の切断廃棄物断片から得られた高い数量の長所を持つBi_2Te_3基づくバルク【Powered by NICT】

Bi₂Te₃ based bulks with high figure of merit obtained from cut waste fragments of cooling crystal rods

著者 (20件)： Xiang Qiusheng (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Xiang Qiusheng (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Fan Xi’an (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Fan Xi’an (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Han Xuewu (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Han Xuewu (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Zhang Chengcheng (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Zhang Chengcheng (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Hu Jie (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Hu Jie (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Feng Bo (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Feng Bo (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Jiang Chengpeng (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Jiang Chengpeng (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Li Guangqiang (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Li Guangqiang (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Li Yawei (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  Li Yawei (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China) ,  He Zhu (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan 430081, China) ,  He Zhu (Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China)
資料名： Materials Chemistry and Physics  (Materials Chemistry and Physics)
巻： 201  ページ： 57-62  発行年： 2017年 
JST資料番号： E0934A  ISSN： 0254-0584  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Bi_2Te_3基づく切削廃棄物断片はp型Bi_2Te_3系熱電材料を調製するために真空冶金技術によりリサイクルした。洗浄,真空冶金,成分調整,第二製錬と抵抗プレス加工焼結(RPS)プロセスにより,Bi_0 4Sb_1 6Te_3バルクを得ることに成功した。全ての証拠は,Sb_2O_3など線切断プロセスからの不純物の大部分は本研究で用いた洗浄,真空冶金プロセスにより除去できることを確認し,リサイクル収率は98%に達した。キャリア含量及び対応する熱電特性は適切な成分調整処理により効果的に調整できた。最後に,Bi_0 4Sb_1 6Te_3バルクが得られ,その無次元性能指数(ZT)は379Kで1.07に達し,平均ZT値は湿式化学冶金法による単一元素Bi,Sb,Teのリサイクルの伝統的プロセスと比較して299Kから1.0以上であった419Kでは,ここで紹介した真空冶金リサイクル技術は3R(リデュース,リユース,リサイクル)の原則に,低コスト,低難易度,低排出,高環境保護と高効率によって特徴づけられる一致であり,精製したインゴットは,高性能熱電材料の生産のための原料として直接用いることができる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 切削 ,  プレス ,  プレス加工 ,  環境保全 ,  熱電材料 ,  焼結 ,  *結晶 ,  性能指数 ,  真空冶金 ,  不純物 ,  *廃棄物 ,  インゴット ,  冶金 ,  リサイクル
準シソーラス用語： 高効率 , 【Automatic Indexing@JST】

著者キーワード (5件)： 熱電性能 ,  Bi_2Te_3 ,  廃棄物切断 ,  リサイクル ,  抵抗プレス焼結