GELATIN/BATIO_3コアシェル複合粒子の調製と電界応答性能の研究【JST・京大機械翻訳】

Preparation and Electro Response of Gelatin/BaTiO_3 Core-shell Composite Particles

著者 (5件)： Yang Xiaolei (Key Laboratory of Applied Surface and Colloid Chemistry Ministry of Education, College of Chemistry & Chemical Engineering, Shaanxi Normal University) ,  Lu Yaping (Key Laboratory of Applied Surface and Colloid Chemistry Ministry of Education, College of Chemistry & Chemical Engineering, Shaanxi Normal University) ,  Gao Meixiang (Yulin Vocational and Technical College) ,  Xie Zunyuan (Key Laboratory of Applied Surface and Colloid Chemistry Ministry of Education, College of Chemistry & Chemical Engineering, Shaanxi Normal University) ,  Gao Lingxiang (Key Laboratory of Applied Surface and Colloid Chemistry Ministry of Education, College of Chemistry & Chemical Engineering, Shaanxi Normal University)
資料名： Wuji Cailiao Xuebao  (Wuji Cailiao Xuebao)
巻： 31  号： 12  ページ： 1306-1310  発行年： 2016年 
JST資料番号： C2432A  ISSN： 1000-324X  CODEN： WCXUET  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 平均粒径0.7~0.9MMのゼラチン(GELATIN)ミクロスフェアを鋳型とし、配向堆積法により、GELATINをコアとし、BATIO_3をシェルとするGELATIN/BATIO_3コアシェル複合粒子を調製した。TEM,XRD,FT-IR,TG,および光学接触角測定を用いて,複合粒子のモルフォロジー,構造,組成,および表面親水性を研究した。その結果,複合粒子は球状粒子であり,良好な表面親水性と分散安定性を有し,BATIO_3シェルは粒子の全質量の18.8%を占め,立方晶相構造を有することが分かった。粒子をヒドロゲル中に分散させ、/電の作用下で得られたエラストマーの貯蔵弾性率を測定し、複合粒子のエラストマー中での電界応答性能を考察した。GELATIN/BATIO_3複合粒子の電界応答性能は純粋BATIO_3粒子のそれよりも強いことが分かった。これらの結果は,BATIO_3被覆が,BATIO_3粒子の電場応答特性を著しく改善することを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： モルフォロジー ,  ヒドロゲル ,  ゼラチン ,  応答特性 ,  親水性 ,  ミクロスフェア ,  *電場 ,  動弾性係数 ,  接触角 ,  *コアシェル構造 ,  エラストマ ,  分散安定性 ,  球状粒子 ,  平均粒子径 ,  *複合粒子

著者キーワード (3件)： core-shell composite particles ,  Gelatin/BaTiO_3 ,  electro response

分類 (3件)： 強誘電体,反強誘電体,強弾性  (BM05030B) ,  コロイド化学一般  (CB11010C) ,  炭素とその化合物  (YB02060D)

タイトルに関連する用語 (6件)： コアシェル ,  複合粒子 ,  調製 ,  電界 ,  応答 ,  研究