広範囲の引張強さを持つ球状黒鉛鋳鉄の旋削加工における被覆工具の摩耗機構【Powered by NICT】

Wear mechanism of coated tools in the turning of ductile cast iron having wide range of tensile strength

著者 (7件)： Martinez Israel (Graduate School of Engineering, Hiroshima University, Hiroshima, Japan) ,  Tanaka Ryutaro (Graduate School of Engineering, Hiroshima University, Hiroshima, Japan) ,  Yamane Yasuo (Graduate School of Engineering, Hiroshima University, Hiroshima, Japan) ,  Sekiya Katsuhiko (Graduate School of Engineering, Hiroshima University, Hiroshima, Japan) ,  Yamada Keiji (Graduate School of Engineering, Hiroshima University, Hiroshima, Japan) ,  Ishihara Tadahiro (Daihatsu metal Co., Ltd. Izumo, Shimane, Japan) ,  Furuya Satoshi (Shimane Institute for Industrial Technology, Matsue, Shimane, Japan)
資料名： Precision Engineering  (Precision Engineering)
巻： 47  ページ： 46-53  発行年： 2017年 
JST資料番号： A0734B  ISSN： 0141-6359  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では摩耗機構と性能を調べるために,400MPaから675MPaまでの引張強さランキングと球状黒鉛鋳鉄の異なる試験片はK15炭化,TiN被覆及びTiAlN被覆工具で旋削したた。切削力と切削温度は両被覆工具の類似していたが逃げ面摩耗とBUEは,TiAlN被覆工具に最も低く,この理由からTiAlN被覆工具は延性鋳鉄の加工に適している。提案した工具摩耗メカニズムは,付着による軟弱黒鉛うつ病摩耗硬いマトリックスから通過することに起因するような断続切削に基づいている。コーテッド工具の逃げ面摩耗の解析は通常の線形スケールの代わりに対数スケールでの摩耗曲線を用いて提案した。このようにして,摩耗速度の変化は容易に観察された。この現象は,被覆層の摩耗と関連していた。切れ刃上の被覆層の部分的損失はEDSマッピング画像およびSEM写真により確認した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 切れ刃 ,  *被覆 ,  *球状黒鉛鋳鉄 ,  *摩耗 ,  *旋削 ,  摩耗速度 ,  工具摩耗 ,  切削抵抗 ,  *被覆工具 ,  被覆層 ,  *引張強さ ,  逃げ面摩耗 ,  切削温度 ,  窒化チタン ,  *摩耗機構 ,  *機械的性質 ,  *性質 ,  *強度

著者キーワード (5件)： ダクタイル鋳鉄 ,  被覆ツール ,  摩耗機構 ,  切削力 ,  切削温度

分類 (4件)： 切削一般  (QC02010V) ,  セラミック材料試験  (HB04000M) ,  炭素とその化合物  (YB02060D) ,  旋削,中ぐり  (QC02020G)

タイトルに関連する用語 (5件)： 引張強さ ,  球状黒鉛鋳鉄 ,  旋削加工 ,  被覆工具 ,  摩耗