超臨界水に曝露された316Lステンレス鋼の腐食と応力腐食割れ感受性に関する研究【Powered by NICT】

A research on the corrosion and stress corrosion cracking susceptibility of 316L stainless steel exposed to supercritical water

著者 (6件)： Guo Xianglong (School of Nuclear Science and Engineering, Shanghai JiaoTong University, NO. 800 Dongchuan Road, Shanghai, China) ,  Chen Kai (School of Nuclear Science and Engineering, Shanghai JiaoTong University, NO. 800 Dongchuan Road, Shanghai, China) ,  Gao Wenhua (School of Nuclear Science and Engineering, Shanghai JiaoTong University, NO. 800 Dongchuan Road, Shanghai, China) ,  Shen Zhao (Department of Materials Science, University of oxford,Parks Road, Oxford OX1 3PH, UK) ,  Lai Ping (School of Nuclear Science and Engineering, Shanghai JiaoTong University, NO. 800 Dongchuan Road, Shanghai, China) ,  Zhang Lefu (School of Nuclear Science and Engineering, Shanghai JiaoTong University, NO. 800 Dongchuan Road, Shanghai, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 127  ページ： 157-167  発行年： 2017年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,550°Cと600°Cの超臨界水に曝露した316Lステンレス鋼の腐食と応力腐食割れ感受性を調べた。XRD,SEM,EDSおよびEBSD分析は試験した試料の微細構造を特性化するために実施した。結果は,試験温度の上昇316L SSの腐食およびSCC抵抗性を低下させることを示した。腐食した試験片の酸化物スケールは二本鎖構造を示し,破壊解析はFe-Crスピネル層におけるFe_3O_4「チャネル」の形成は,550°Cと600°CのSCW中の材料の粒界および粒内SCCに寄与することを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *応力腐食割れ ,  結晶粒界 ,  微細構造 ,  *感受性 ,  *腐食 ,  キャラクタリゼーション ,  *超臨界水 ,  スピネル ,  X線回折 ,  チャネル ,  酸化物
準シソーラス用語： 破壊解析 ,  試験温度 ,  EBSD ,  *SUS316L , 【Automatic Indexing@JST】

著者キーワード (5件)： 316Lステンレス鋼 ,  超臨界水 ,  微細構造特性化 ,  腐食 ,  応力腐食割れ

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (7件)： 超臨界水 ,  曝露 ,  316Lステンレス鋼 ,  腐食 ,  応力腐食 ,  割れ感受性 ,  研究