Ndの性質に及ぼす粉末結晶度とその影響の促進:YAG透明セラミック【Powered by NICT】

Promotion of powder crystallinity and its influence on the properties of Nd:YAG transparent ceramics

著者 (6件)： Ma Benyuan (College of Physics and Electronic Engineering, Nanyang Normal University, Nanyang 473061, China) ,  Wang Bin (Physics and Electronic Engineering Department, Xinxiang University, Xinxiang 453003, China) ,  Zhang Wei (Southwest Institute of Technical Physics, Chengdu 610064, China) ,  Wei Nian (Department of Physics and Key Laboratory for Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  Lu Tiecheng (Department of Physics and Key Laboratory for Radiation Physics and Technology of Ministry of Education, Sichuan University, Chengdu 610064, China) ,  He Junbao (College of Physics and Electronic Engineering, Nanyang Normal University, Nanyang 473061, China)
資料名： Optical Materials  (Optical Materials)
巻： 64  ページ： 384-390  発行年： 2017年 
JST資料番号： W0468A  ISSN： 0925-3467  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Nd:種々の結晶度のYAG原料粉末を1100 1250°Cでか焼し2 6により共沈前駆体から得られた。XRD,HRTEMおよびEDXを用いて,粉末結晶度,例えば,その相,格子定数の変化,表面欠陥と形態を分析した。その後セラミックスを種々の粉末結晶度の初期固有効果を比較に1780°Cで10時間の簡単な真空焼結により作製した。セラミックの誘起欠陥状態と対応する特性を調べ,考察した。結果は十分に結晶化した粉末は粒子表面,良く結晶化しない厚い層を含むがXRD検出を逃れることができることを示した。貧弱に結晶化した粉末は,不均一セラミック焼結を貢献し,さらに最終セラミック中の欠陥,例えば,不純相介在物と転位を紹介した。結果は,粉末結晶度は促進し,セラミック特性を改善するためのさらなる方法として考慮すべきであることを明らかにした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 格子定数 ,  *セラミック ,  焼結 ,  前駆体 ,  *ネオジム ,  表面欠陥 ,  介在物 ,  X線回折 ,  *粉体 ,  か焼 ,  *結晶度 ,  結晶化 ,  共沈
準シソーラス用語： 真空焼結 ,  HRTEM , 【Automatic Indexing@JST】

著者キーワード (5件)： 透明セラミック ,  共沈 ,  粉末結晶度 ,  表面欠陥 ,  焼結

分類 (3件)： 無機化合物のルミネセンス  (BM08093J) ,  セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (7件)： Nd ,  性質 ,  粉末 ,  結晶度 ,  促進 ,  YAG ,  セラミック