冷間圧延した連続鋳造AA2037アルミニウム合金における集合組織発達に及ぼす析出状態の影響【Powered by NICT】

Effect of precipitation state on texture evolution in cold-rolled continuous cast AA 2037 aluminum alloy

著者 (4件)： Zhang J.X. (Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao, 066004, China) ,  Liu C. (Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao, 066004, China) ,  Liu W.C. (Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao, 066004, China) ,  Man C.-S. (Department of Mathematics, University of Kentucky, 715 Patterson Office Tower, Lexington, KY 40506, USA)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 728  ページ： 1199-1208  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 冷間圧延中の連続鋳造(CC)AA2037アルミニウム合金の集合組織の変化を,析出状態の関数としてX線回折により調べた。結果は時効中に生成した種々の析出物は立方体+r-cube成分の消失の速度を減少させ,同速度は時効時間の増加と共に減少することを示した。大きいひずみにおいてθ′とθ析出物は成分の消失,残り方位をもつ結晶粒中に形成されたせん断帯が集合組織の発達を加速することを意味する速度を有意に高めた。析出状態はβ繊維に沿って配向強度の分布に顕著に影響を及ぼす。時効時間の増加に伴い,より多くの初期立方方位結晶粒は圧下率の増加とともにC配向よりもむしろB方位,C配向の強度の急激な増加をもたらすに回転した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶粒 ,  *アルミニウム合金 ,  析出物 ,  *集合組織 ,  *連続鋳造 ,  X線回折 ,  剪断帯 ,  *冷間圧延 ,  圧下率 ,  時効
準シソーラス用語： 六面体 , 【Automatic Indexing@JST】

著者キーワード (5件)： アルミニウム合金 ,  冷間圧延 ,  沈殿 ,  テクスチャ ,  X線回折

分類 (2件)： 組織的硬化現象  (WB01020C) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： 冷間圧延 ,  連続鋳造 ,  アルミニウム合金 ,  集合組織 ,  発達 ,  析出