ジルコニウム合金の低温圧延強化された不均一変形と再結晶粒成長【Powered by NICT】

Cryo-rolling enhanced inhomogeneous deformation and recrystallization grain growth of a zirconium alloy

著者 (7件)： He Weijun (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Chen Xin (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Liu Na (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Luan Baifeng (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China) ,  Yuan Gaihuan (State Nuclear Baoti Zirconium Industry Co., Ltd., Baoji 721014, China) ,  Yuan Gaihuan (Shanxi Key Laboratory of Nuclear Grade Zirconium, Baoji 721014, China) ,  Liu Qing (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 699  ページ： 160-169  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究は六方晶Zr合金のその後の再結晶に及ぼす極低温圧延の影響に焦点を当てた。初期再結晶化したミクロ組織で,作製したZrシートは液体窒素温度(LNT)と室温(RT)で圧延した。各圧延温度のために,二レベル歪の20%と40%,を適用した。,受け取ったままと圧延板を含む試料を700°Cでアニールした3分,5分であった。変形し,焼なましたZr試料のミクロ組織を,電子後方散乱回折(EBSD)法によって詳細に特性化した。圧延後,双晶ラメラはZr試料では観測されない。極低温圧延における不均一変形の強度はRT圧延よりもより厳しいことが分かった。アニーリング後,Zrの再結晶平均粒径は変形温度で適用歪の増加と共に減少した。与えられた圧下率では,再結晶した平均粒径は変形温度の低下と共に増加した。Zrの集合組織方位は圧延変形と焼なましプロセス中に大きく変化しなかった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 圧下率 ,  圧延温度 ,  焼なまし ,  極低温 ,  *ジルコニウム合金 ,  集合組織 ,  *ジルコニウム ,  *低温 ,  粒径 ,  *圧延 ,  双晶 ,  *再結晶
準シソーラス用語： 変形温度 ,  EBSD ,  *不均一変形 , 【Automatic Indexing@JST】

著者キーワード (5件)： ジルコニウム合金 ,  再結晶 ,  低温圧延 ,  粒径 ,  不均一変形

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： ジルコニウム合金 ,  低温 ,  圧延 ,  強化 ,  不均一変形 ,  結晶粒成長