そのガラス転移温度以下でのNi_60Nb_30Ta_10金属ガラスの酸化挙動【Powered by NICT】

Oxidation behaviour of Ni₆₀Nb₃₀Ta₁₀ metallic glass below its glass transition temperature

著者 (6件)： Poddar Chiranjit (Homi Bhabha National Institute (HBNI), Mumbai, India) ,  Poddar Chiranjit (Corrosion Science and Technology Division, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603 102, India) ,  Jayaraj J. (Corrosion Science and Technology Division, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603 102, India) ,  Mallika C. (Corrosion Science and Technology Division, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603 102, India) ,  Kamachi Mudali U. (Homi Bhabha National Institute (HBNI), Mumbai, India) ,  Kamachi Mudali U. (Corrosion Science and Technology Division, Indira Gandhi Centre for Atomic Research, Kalpakkam, 603 102, India)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 728  ページ： 1146-1152  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 空気中Ni_60Nb_30Ta_10金属ガラスの酸化挙動を,そのガラス転移温度(665 °C)以下で調べた。酸化速度は450と550°Cで2段階放物線速度則に従った。放物線速度定数は酸化温度の上昇と共に増加した。450°Cでは,主にNb_2O_5とTa_2O_5,微量のNiOとNi_2O_3の薄い非晶質酸化物膜は表面上に観察された。550°Cでは,酸化は表面に対する微量金属NiのNi~2+とNi~3+イオン厚い酸化物層が成長したが,広範な立方晶NiO及び単斜晶Ni_2O_3含むの外側への拡散を誘導した。興味深いことに,550°CでNb_2O_5とTa_2O_5酸化物は酸化層の表面には完全に消失した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *ニッケル ,  非晶質 ,  酸化物 ,  X線光電子分光法 ,  *金属ガラス ,  酸化層 ,  酸化膜 ,  *ガラス転移点 ,  *酸化 ,  単斜晶系
準シソーラス用語： 酸化物層 ,  微量金属 ,  速度定数 ,  酸化速度 ,  *酸化挙動 , 【Automatic Indexing@JST】

著者キーワード (6件)： 金属ガラス ,  酸化 ,  酸化物層 ,  Kinetics ,  拡散 ,  X線光電子分光法

分類 (2件)： 腐食  (WB03030B) ,  非晶質金属の構造  (BK04020D)

タイトルに関連する用語 (3件)： ガラス転移温度 ,  金属ガラス ,  酸化挙動