イリドNi_1Co-を含む陽極酸化アルミニウム膜の作製と特性評価【Powered by NICT】

Preparation and characterization of iridescent Ni_1- Co -containing anodic aluminum oxide films

著者 (9件)： Xu Qin (Department of Applied Physics, Hebei University of Technology, Tianjin 300401, China) ,  Sun Chun-Xin (Department of Applied Physics, Hebei University of Technology, Tianjin 300401, China) ,  Wang Zhi-Jun (Hebei Chemical and Pharmaceutical Vocational Technology College, Shijiazhuang 050026, China) ,  Liu Jing-Jin (Faculty of Science, Tianjin University, Tianjin 300072, China) ,  Ren Ya-Xuan (Department of Applied Physics, Hebei University of Technology, Tianjin 300401, China) ,  Hao Sheng-Zhen (Department of Applied Physics, Hebei University of Technology, Tianjin 300401, China) ,  Zhu Ji-Liang (Department of Applied Physics, Hebei University of Technology, Tianjin 300401, China) ,  Sun Yu-Bao (Department of Applied Physics, Hebei University of Technology, Tianjin 300401, China) ,  Sun Hui-Yuan (College of Physics Science & Information Engineering, Hebei Normal University, Shijiazhuang 050024, China)
資料名： Dyes and Pigments  (Dyes and Pigments)
巻： 147  ページ： 313-317  発行年： 2017年12月 
JST資料番号： D0966B  ISSN： 0143-7208  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,明るい構造色を持つNiCo@PAA複合膜は,AC電着により作製することに成功し,それらの光学的および磁気的性質を調べた。反射スペクトル試験の結果は,著者らの実験で観察されたものと一致していることが分かった,NiCo合金ナノワイヤのアスペクト比は走査電子顕微鏡の結果により示された非常に小さく,磁石試験の結果が示すように,NiCo合金ナノワイヤは,ナノワイヤの方向と平行である容易磁化方向を持ち,保磁力はCo含有量の増加とともにゆっくりと増加すると保磁力は,低温で増加し,NiCo合金ナノワイヤの磁化反転機構はコヒーレント回転モデルと一致した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *酸化アルミニウム ,  ニッケル合金 ,  コバルト添加合金 ,  酸化膜 ,  *色
準シソーラス用語： *アノード酸化アルミニウム ,  虹色 ,  *構造色

著者キーワード (4件)： NiCo合金 ,  ナノワイヤ ,  AC電着 ,  磁気特性

分類 (2件)： 化成処理  (WC08050J) ,  光物性一般  (BM08010A)

タイトルに関連する用語 (5件)： イリド ,  陽極酸化 ,  アルミニウム膜 ,  作製 ,  特性評価