ホットプレスによって作製したチタン/アルミニウム積層複合材料の特性評価と成形性

Characterization and Formability of Titanium/Aluminum Laminate Composites Fabricated by Hot Pressing

著者 (9件)： QIN Liang (Nanjing Univ. Aeronautics and Astronautics, Nanjing, CHN) ,  QIN Liang (Jiangsu Univ. Sci. and Technol., Zhangjiagang, CHN) ,  WANG Hui (Nanjing Univ. Aeronautics and Astronautics, Nanjing, CHN) ,  CUI Shengqiang (Nanjing Univ. Aeronautics and Astronautics, Nanjing, CHN) ,  WU Qian (Nanjing Univ. Aeronautics and Astronautics, Nanjing, CHN) ,  FAN Minyu (Nanjing Univ. Aeronautics and Astronautics, Nanjing, CHN) ,  YANG Zonghui (Jiangsu Key Lab. of Advanced Structural Materials and Application Technol., Nanjing, CHN) ,  TAO Jie (Nanjing Univ. Aeronautics and Astronautics, Nanjing, CHN) ,  TAO Jie (Jiangsu Key Lab. of Advanced Structural Materials and Application Technol., Nanjing, CHN)
資料名： Journal of Materials Engineering and Performance  (Journal of Materials Engineering and Performance)
巻： 26  号： 7  ページ： 3579-3587  発行年： 2017年07月 
JST資料番号： C0161B  ISSN： 1059-9495  CODEN： JMEPEG  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： Ti/Al積層材の成形性を単軸引張試験,限界絞り比(LDR)及び成形限界線図(FLC)によって評価した。厚さ0.1mmのTi(TA1)及びAl(1060)箔を交互に計11層重ね,真空中で550°C,3MPaの圧力で接合した。接合界面の形態と元素分布をSEM-EDSによって測定した。積層材の引張試験を10^-2,10^-3及び10^-4s^-1の歪み速度で行った。積層材,Ti板及びAl板の深絞り試験を行い,LDRを求めた。ドット格子を印刷した積層材,Ti及びAl板のFLC試験を行った。ホットプレスによって良好な接合界面の積層材が出来た。積層材の最適な構成方程式を提案した。積層材のLDRは1.8であった。積層材のFLCはAlとTiの中間の0.31であった。LDR及びFLC試験における亀裂発生について述べた。

シソーラス用語： ホットプレス ,  *チタン ,  *アルミニウム ,  純金属 ,  *積層材料 ,  複合材料 ,  金属箔 ,  厚み ,  加熱温度 ,  圧力 ,  界面 ,  接合部 ,  元素分析 ,  引張試験 ,  歪速度 ,  深絞り加工 ,  *成形性 ,  比率 ,  成形限界線図 ,  構成方程式 ,  亀裂発生
準シソーラス用語： 限界絞り比

分類 (2件)： クラッド材  (WE04020G) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： ホットプレス ,  作製 ,  チタン ,  アルミニウム ,  積層複合材料 ,  特性評価 ,  成形性