ジルコニウム酸バリウム中に誘起された欠陥双極子の定義されたナノスケール強誘電極性秩序【Powered by NICT】

Defect-dipole defined nanoscale ferroelectric polar-orders induced in Barium Zirconate

著者 (7件)： Dutta Moumita (Department of Electrical and Computer Engineering, University of Texas at San Antonio, San Antonio, TX 78249, USA) ,  Ding Ying (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Ding Ying (Department of Physics and Astronomy, University of Texas at San Antonio, San Antonio, TX 78249, USA) ,  Chen Jianghua (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Chen Chonglin (Department of Physics and Astronomy, University of Texas at San Antonio, San Antonio, TX 78249, USA) ,  Bhalla Amar (Department of Electrical and Computer Engineering, University of Texas at San Antonio, San Antonio, TX 78249, USA) ,  Guo Ruyan (Department of Electrical and Computer Engineering, University of Texas at San Antonio, San Antonio, TX 78249, USA)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 130  ページ： 119-123  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ナノスケール強誘電挙動は,酸素欠乏環境で成長させたエピタキシャルBaZrO_3薄膜で調べた。本質的に中心対称が,顕著な強誘電分極状態を圧電力顕微鏡(PFM)により観測された,逆分極した場合達成された偏光スイッチングを示した。固有極性方向の欠如は,むしろ観察されたナノスケール極性秩序を,膜成長中に導入された酸素空格子点に起因する欠陥双極子への構造非対称性と歪のような強誘電性の従来の根本原因を排除した。表面電位の不均一分布を示す静電気力顕微鏡(EFM)を測定し分極に寄与する酸素空孔の蓄積を確認した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 酸素欠乏 ,  表面電位 ,  非対称性 ,  圧電気 ,  *極性 ,  強誘電性 ,  力顕微鏡 ,  対称性 ,  分極
準シソーラス用語： 静電力顕微鏡 ,  酸素空格子点 ,  強誘電分極 ,  *ナノスケール ,  *欠陥双極子 ,  *ジルコニウム酸バリウム , 【Automatic Indexing@JST】

著者キーワード (4件)： 強誘電材料 ,  薄膜 ,  空格子点 ,  走査型プローブ顕微鏡(SPM)