ZnOの作製:NiナノワイヤとそれらのRamanスペクトル【Powered by NICT】

Fabrication of ZnO:Ni nanowires and their Raman spectra

著者 (4件)： Zhang Jun (Key Laboratory of Optoelectronic Information Techniques of Shandong, Institute Optoelectronic Information Science & Techniques, Yantai University, Yantai 264005, PR China) ,  Jiang Feihong (Key Laboratory of Optoelectronic Information Techniques of Shandong, Institute Optoelectronic Information Science & Techniques, Yantai University, Yantai 264005, PR China) ,  Yang Yongdong (Key Laboratory of Optoelectronic Information Techniques of Shandong, Institute Optoelectronic Information Science & Techniques, Yantai University, Yantai 264005, PR China) ,  Sui Chenhong (Key Laboratory of Optoelectronic Information Techniques of Shandong, Institute Optoelectronic Information Science & Techniques, Yantai University, Yantai 264005, PR China)
資料名： Materials Letters  (Materials Letters)
巻： 195  ページ： 136-138  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ZnO:Niナノワイヤを高温の気相-固相堆積プロセスにより作製した。調製されたままの試料の形態を走査型電子顕微鏡によって特性化した。室温Ramanスペクトルは,系中の格子欠陥の存在を示した。ドープしていないZnOと付加的なモードの振動モードは,NiをドープしたZnOナノワイヤのRamanスペクトルで観察した。437.2cm~ 1でE_2~高最も強いモードはZnO:Niナノワイヤは六方晶(ウルツ鉱型)構造を保つことを示した。656.6cm~ 1でのモードはホスト欠陥による局所的振動モードに帰した。Niドープは254.1~540.6cm~ 1で二つの付加的モードの出現をもたらした。これらのモードは,表面フォノンモードに帰属でき,Raman散乱ピークは欠陥を形成するNiドーピングに起因するであろう。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 振動モード ,  キャラクタリゼーション ,  *酸化亜鉛 ,  Raman散乱 ,  *ニッケル ,  気相 ,  格子欠陥 ,  *ナノワイヤ ,  固相 ,  局在振動 ,  ドーピング ,  *Ramanスペクトル ,  六方晶系 ,  走査電子顕微鏡 ,  表面フォノン

著者キーワード (4件)： ナノ結晶材料 ,  Ramanスペクトル ,  化学蒸着 ,  ZnO:Niナノワイヤ

分類 (4件)： 塩基,金属酸化物  (CD01030Z) ,  半導体のルミネセンス  (BM08092S) ,  酸化物薄膜  (BK14050P) ,  無機化合物の赤外スペクトル及びRaman散乱,Ramanスペクトル  (BM08063C)

タイトルに関連する用語 (5件)： ZnO ,  作製 ,  Ni ,  ナノワイヤ ,  Ramanスペクトル