Ca_2GeO_4:Cr~4+透明ナノガラスセラミック【Powered by NICT】

Ca₂GeO₄:Cr⁴⁺ transparent nano-glass ceramics

著者 (7件)： Ivanov V.A. (N.I. Lobachevsky State University of Nizhni Novgorod, Nizhni Novgorod 603950, Russia) ,  Simanovskiy D.V. (N.I. Lobachevsky State University of Nizhni Novgorod, Nizhni Novgorod 603950, Russia) ,  Marychev M.O. (N.I. Lobachevsky State University of Nizhni Novgorod, Nizhni Novgorod 603950, Russia) ,  Andreev P.V. (N.I. Lobachevsky State University of Nizhni Novgorod, Nizhni Novgorod 603950, Russia) ,  Koseva I. (Bulgarian Academy of Science, Institute of General and Inorganic Chemistry, BU-1113 Sofia, Bulgaria) ,  Tzvetkov P. (Bulgarian Academy of Science, Institute of General and Inorganic Chemistry, BU-1113 Sofia, Bulgaria) ,  Nikolov V. (Bulgarian Academy of Science, Institute of General and Inorganic Chemistry, BU-1113 Sofia, Bulgaria)
資料名： Journal of Non-Crystalline Solids  (Journal of Non-Crystalline Solids)
巻： 456  ページ： 76-82  発行年： 2017年 
JST資料番号： D0642A  ISSN： 0022-3093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究の目的は,合成の適正条件を持つCr~4+Ca_2GeO_4ナノ相のガラスセラミックを得ることを可能にする透明なガラスセラミックの要求を満たすガラス組成を見出すことであった。三系列のガラス組成を検討した,CaO,GeO_2とガラス形成体:CaO GeO_2~-B_2O_3,CaO GeO_2~-Na_2B_4O_7とCaO GeO_2~-LiBO_2を含んでいた。三システム間の比較は,CaO GeO_2~-LiBO_2は相ガラスにCa_2GeO_4ナノ相,ガラスの融解と均質化(1100 1150°C)の温度およびCa_2GeO_4を得る可能性に関して,含むガラスセラミックを得るための有意に良好な条件を提供することを明確に示した。核の速度と粒子成長の速度間の大きな差のために,高い結晶化度で約50nmの粒子が受けられることを確立した。透過および光ルミネセンススペクトルを測定し,活性イオンはCr~4+であることを示した。1000~1600nmの範囲の発光の広帯域を確立した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 均質化 ,  イオン ,  *ガラスセラミック ,  広帯域 ,  *ガラス ,  結晶度 ,  ガラス成形
準シソーラス用語： 光ルミネセンススペクトル ,  粒子成長 , 【Automatic Indexing@JST】

著者キーワード (4件)： 相図 ,  ガラスセラミック ,  Cr~4+Ca_2GeO_4ナノ相 ,  光学スペクトル

分類 (2件)： ガラスの性質・分析・試験  (YC02030Z) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (1件)： ガラスセラミック