ウシヒドロキシアパタイトの機械的性質に及ぼすムライト添加の焼結効果【Powered by NICT】

Sintering effects of mullite-doping on mechanical properties of bovine hydroxyapatite

著者 (7件)： Yetmez M. (Department of Mechanical Engineering, Bulent Ecevit University, 67100 Zonguldak, Turkey) ,  Erkmen Z.E. (Department of Metallurgical and Materials Engineering, Marmara University, 34722 Istanbul, Turkey) ,  Kalkandelen C. (Biomedical Engineering Program, Graduate School of Natural and Applied Sciences, Istanbul University, 34320 Istanbul, Turkey) ,  Kalkandelen C. (Vocational School of Technical Sciences, Biomedical Devices Technology Department, Istanbul University, 34320 Istanbul, Turkey) ,  Ficai A. (Faculty of Applied Chemistry and Material Science, Politechnica University of Bucharest, Bucharest, Romania) ,  Oktar F.N. (Department of Bioengineering, Faculty of Engineering, Marmara University, 34722 Istanbul, Turkey) ,  Oktar F.N. (Advanced Nanomaterials Research Laboratory, Marmara University, 34722 Istanbul, Turkey)
資料名： Materials Science & Engineering. C. Materials for Biological Applications  (Materials Science & Engineering. C. Materials for Biological Applications)
巻： 77  ページ： 470-475  発行年： 2017年 
JST資料番号： W0574A  ISSN： 0928-4931  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,粉末ムライトをドープしたウシ誘導ヒドロキシアパタイトの微細構造挙動に及ぼす焼結効果は1000°Cと1300°Cの間の温度範囲で検討した。結果は,圧縮強度とミクロ硬さの両方の最大値は1200°Cで焼結した5%,7.5%,10と12.5wt%のすべてのムライト添加試料で達成されることを示した。さらに,1000°C以上では,HAの分解とゲーレナイトのような新しい相形成は10wt%までムライト強化を増加させる圧縮強さと微小硬さ特性の両方において主要な役割を果たす。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 微細構造 ,  粉体 ,  *機械的性質 ,  ドーピング ,  圧縮強さ ,  *ムライト ,  *ヒドロキシアパタイト ,  微小硬さ ,  *焼結
準シソーラス用語： 相形成 ,  ゲーレナイト ,  温度範囲 , 【Automatic Indexing@JST】

著者キーワード (4件)： 焼結 ,  機械的性質 ,  ウシ由来ヒドロキシアパタイト ,  ムライト

分類 (1件)： 医用素材  (GA05040H)