張力下のグラフェンシートにおける片側予亀裂の成長速度【Powered by NICT】

Growth speed of single edge pre-crack in graphene sheet under tension

著者 (5件)： Hua Jun (Department of Engineering Mechanics, School of Science, Xi’an University of Architecture and Technology, Xi’an 710055, PR China) ,  Liu Qinlong (Department of Engineering Mechanics, School of Science, Xi’an University of Architecture and Technology, Xi’an 710055, PR China) ,  Hou Yan (Department of Engineering Mechanics, School of Science, Xi’an University of Architecture and Technology, Xi’an 710055, PR China) ,  Wu Xiaxia (Department of Engineering Mechanics, School of Science, Xi’an University of Architecture and Technology, Xi’an 710055, PR China) ,  Zhang Yuhui (Department of Engineering Mechanics, School of Science, Xi’an University of Architecture and Technology, Xi’an 710055, PR China)
資料名： Engineering Fracture Mechanics  (Engineering Fracture Mechanics)
巻： 182  ページ： 337-355  発行年： 2017年 
JST資料番号： A0119A  ISSN： 0013-7944  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 分子動力学シミュレーションには一定歪速度で引張下での亀裂発生前の単層アームチェア型における亀裂伝搬を研究するために使用される。グラフェンの表面自由エネルギーは5.1J/m~2であり,応力拡大係数は3.2MPa mであることが分かった。しかし亀裂速度は亀裂成長過程での一定でない。亀裂速度の限界は8400m/sである。亀裂速度は,初期亀裂長さとひずみ載荷速度の両方に依存する。初期亀裂長さが短くなると,亀裂速度速かった。より高いひずみ載荷速度は亀裂速度を向上させることができるが,最大速度は限界速度を超えることができない。初期亀裂長さの増加に伴って,初期亀裂長さの影響を減少し,歪負荷速度効果は増加した。さらに,ひずみ載荷速度の影響は主に亀裂伝搬中に活性化されることが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *予亀裂 ,  引張 ,  *成長速度 ,  載荷速度 ,  亀裂発生 ,  *張力 ,  分子動力学 ,  応力拡大係数 ,  *グラフェン ,  *亀裂 ,  歪速度 ,  臨界速度 ,  亀裂伝搬
準シソーラス用語： 亀裂長さ ,  分子動力学シミュレーション , 【Automatic Indexing@JST】

著者キーワード (4件)： グラフェン ,  分子動力学 ,  破壊 ,  亀裂速度