エレクトロスピニングによる銅輝コバルト鉱(CuCo_2O_4)繊維の合成と磁気的性質【Powered by NICT】

Synthesis and magnetic properties of copper cobaltite (CuCo₂O₄) fibers by electrospinning

著者 (4件)： Nakhowong Ronariddh (Program of Physics, Faculty of Science, Ubon Ratchathani Rajabhat University, Ubon Ratchathani 34000, Thailand) ,  Nakhowong Ronariddh (Functional Nanomaterials and Electrospinning Research Laboratory, Faculty of Science, Ubon Ratchathani Rajabhat University, Ubon Ratchathani 34000, Thailand) ,  Chueachot Romteera (Program of Chemistry, Faculty of Science, Ubon Ratchathani Rajabhat University, Ubon Ratchathani 34000, Thailand) ,  Chueachot Romteera (Functional Nanomaterials and Electrospinning Research Laboratory, Faculty of Science, Ubon Ratchathani Rajabhat University, Ubon Ratchathani 34000, Thailand)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 715  ページ： 390-396  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 直径500 800nmの銅コバルタイト(CuCo_2O_4)繊維を,エレクトロスピニングプロセス2600 800°Cで焼成の組合せにより合成することに成功した。熱重量分析と示差熱分析の結果は,重量損失は約600°Cで安定であることを示した。X線回折とFourier変換赤外分光の結果は,スピネルCuCo_2O_4の形成を確認し,検出されたCuOの不純物相であった。走査電子顕微鏡と透過電子顕微鏡の結果は,CuCo_2O_4繊維は焼成後のナノ粒子の粗い表面を持つことを明らかにした。振動試料磁力計測定は試料は600 800°Cでフェリ磁性と反強磁性挙動を示すことを決定した。飽和磁化,残留磁化,保磁力,と異方性定数は焼成の増加と共に減少した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 残留磁化 ,  走査電子顕微鏡 ,  熱重量分析 ,  フェリ磁性 ,  スピネル ,  *エレクトロスピニング ,  保磁力 ,  透過型電子顕微鏡 ,  示差熱分析 ,  反強磁性 ,  酸化第二銅 ,  重量損失 ,  飽和磁化
準シソーラス用語： 試料振動型磁力計 ,  *コバルタイト , 【Automatic Indexing@JST】

著者キーワード (4件)： 銅輝コバルト鉱 ,  磁気的性質 ,  繊維技術 ,  エレクトロスピニング

分類 (1件)： 酸化物結晶の磁性  (BM06050E)

タイトルに関連する用語 (5件)： エレクトロスピニング ,  銅 ,  輝コバルト鉱 ,  繊維 ,  磁気的性質