超低温処理による青銅青銅のミクロ組織と性質への影響【JST・京大機械翻訳】

Effect of deep cryogenic treatment on microstructure and properties of aluminum bronze

著者 (6件)： Jin Leilei (School of Materials Science and Engineering,Changzhou University) ,  Wei Kunxia (School of Materials Science and Engineering,Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology) ,  Wang Shenglong (School of Materials Science and Engineering,Changzhou University) ,  Wei Wei (School of Materials Science and Engineering,Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology) ,  Du Qingbo (School of Materials Science and Engineering,Changzhou University) ,  Hu Jing (School of Materials Science and Engineering,Changzhou University, Jiangsu Key Laboratory of Materials Surface Science and Technology)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 10  ページ： 73-78  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 固溶態Lv(CU-2.2%AL,CU-4.5%AL,CU-7%AL)の超低温処理を行った。アルミニウム青銅のミクロ組織,硬さ,および引張特性に及ぼす超低温時間と積層欠陥の影響を研究した。結果は以下を示す。アルミニウム青銅を超低温で処理すると,結晶粒が微細化し,双晶が形成された。CU-2.2%AL,CU-4.5%ALおよびCU-7%ALアルミニウム青銅の硬度は,超低温時間の増加とともに,最初に増加し,次に減少し,最後に,安定し,そして,10~12時間でピークに達した。それらの間で,98.5 HBS,93.7 HBS,96.1 HBS,およびブルセラの硬度と超低温時間の間の関係式を確立した。アルミニウム合金の降伏強さは,超低温時間の延長によって改善されるが,引張強さと均一伸びに及ぼす影響はほとんどない。積層欠陥はCU-2.2%ALとCU-4.5%AL合金の引張強さにほとんど影響を及ぼさなかったが,CU-7%AL合金の引張強さは著しく増加した。降伏強さと均一伸びは,積層エネルギーの低下と共に増加した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 硬度 ,  引張強さ ,  結晶粒 ,  伸び ,  精密化 ,  *青銅 ,  アルミニウム合金 ,  *超低温 ,  双晶 ,  降伏強さ ,  積層欠陥 ,  積層 ,  引張特性 ,  アルミニウム青銅 ,  機械的性質 ,  強度 ,  格子欠陥
準シソーラス用語： アルミニウムブロンズ ,  *低温処理 , 【Automatic Indexing@JST】

著者キーワード (4件)： aluminum bronze ,  deep cryogenic treatment (DCT) ,  microstructure ,  mechanical property

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)