大きく改善された水質浄化性能を有するMOF@GOにより調節した複合限外ろ過膜【Powered by NICT】

Composite ultrafiltration membrane tailored by MOF@GO with highly improved water purification performance

著者 (5件)： Ma Jing (State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China) ,  Guo Xiangyu (State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China) ,  Ying Yunpan (State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China) ,  Liu Dahuan (State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China) ,  Zhong Chongli (State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China)
資料名： Chemical Engineering Journal  (Chemical Engineering Journal)
巻： 313  ページ： 890-898  発行年： 2017年 
JST資料番号： D0723A  ISSN： 1385-8947  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高流束を伴う進行性ろ過膜の開発,良好な溶質排除と優れた防汚性能が求められている。親水性酸化グラフェン(GO)ナノシートは,水精製のための複合膜の調製のための魅力的な充填剤である。しかし,完全に利点を利用し,GOナノシートの欠点を改善できる戦略はまだ必要である。本研究では,UiO-66は多孔質改質剤としてGO層に固定した。取り込まれたUiO-66は効果的に積層からGO層を防ぎ,複合材料(UiO 66@GO)にユニークな特性を導入することができる。一連の新規複合膜が得られUiO 66@GO複合材料とポリエーテルスルホン(PES)を用いて調製した。結果として,調製した複合膜(UiO 66@GO/PES)は高い親水性と水質浄化性能を示した。特に3.0wt%UiO 66@GOを装填した複合材料膜の水フラックスはPESとGO/PES膜のそれと比較してそれぞれ351%と78%の増加を示した。UiO 66@GO/PES膜は良好な溶質排除と印象的な防汚性能,工業用水浄化の応用のための魅力的であることを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 親水性 ,  複合材料 ,  溶質 ,  複合膜 ,  工業用水 ,  多孔性 ,  *浄水 ,  ナノシート ,  防汚性
準シソーラス用語： 水フラックス ,  *限外濾過膜 , 【Automatic Indexing@JST】

著者キーワード (4件)： 金属-有機フレームワーク ,  酸化グラフェン ,  限外ろ過膜 ,  水質浄化

分類 (2件)： 膜分離  (XD02120Z) ,  ポリエーテル  (YH07050T)

タイトルに関連する用語 (3件)： 水質浄化 ,  調節 ,  限外ろ過膜