ワイヤ+アーク付加製造したTi-6Al-4Vの破壊靭性と疲労き裂成長速度特性【Powered by NICT】

Fracture toughness and fatigue crack growth rate properties in wire + arc additive manufactured Ti-6Al-4V

著者 (7件)： Zhang X (School of Aerospace, Transport and Manufacturing, Cranfield University, Bedford MK43 0AL, UK) ,  Zhang X (Faculty of Engineering, Environment & Computing, Coventry University, Coventry CV1 5FB, UK) ,  Martina F (School of Aerospace, Transport and Manufacturing, Cranfield University, Bedford MK43 0AL, UK) ,  Ding J (School of Aerospace, Transport and Manufacturing, Cranfield University, Bedford MK43 0AL, UK) ,  Wang X (School of Aerospace, Transport and Manufacturing, Cranfield University, Bedford MK43 0AL, UK) ,  Wang X (Faculty of Engineering, Environment & Computing, Coventry University, Coventry CV1 5FB, UK) ,  Williams SW (School of Aerospace, Transport and Manufacturing, Cranfield University, Bedford MK43 0AL, UK)
資料名： Fatigue & Fracture of Engineering Materials & Structures  (Fatigue & Fracture of Engineering Materials & Structures)
巻： 40  号： 5  ページ： 790-803  発行年： 2017年 
JST資料番号： H0708A  ISSN： 8756-758X  CODEN： FFESEY  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ワイヤ+アーク付加製造(WAAM)プロセスによって作製したTi-6Al-4Vの破壊と疲れ亀裂成長特性の実験的研究を提示した。最初に,破壊靭性は作製方向に関して二種類の方向で測定した;ワイヤ酸素含有量と構築戦略の影響もミクロ組織検査の観点から評価した。第二に,疲れ亀裂成長速度は完全に付加製造した試料と同様に,WAAMおよび鍛造材料間の界面を含む試料で測定した。後者のカテゴリーは界面に関して亀裂位置と方位の五種類のシナリオをカバーしている。疲労亀裂成長速度は鍛造またはWAAM単独条件のそれと比較した。これら試験の亀裂成長軌跡は微細構造特性に関連して議論される。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 界面 ,  *破壊靱性 ,  微細構造 ,  *付加製造 ,  亀裂 ,  *疲れ亀裂成長速度 ,  鍛造 ,  *金属線 ,  亀裂伝搬 ,  疲れ亀裂成長 ,  材料 ,  *アーク放電 ,  軌跡
準シソーラス用語： 酸素含有量 ,  実験研究 , 【Automatic Indexing@JST】

著者キーワード (5件)： 疲労亀裂成長 ,  破壊靭性 ,  及ぼす金属 ,  チタン ,  ワイヤ+アーク付加製造

分類 (2件)： 金属材料  (HC04020L) ,  材料試験  (HB02020U)

タイトルに関連する用語 (6件)： ワイヤ ,  アーク ,  付加製造 ,  Ti ,  破壊靭性 ,  疲労き裂成長速度