PAN前駆体繊維の熱安定化における半径方向の構造と性質の関係【Powered by NICT】

Radial structure and property relationship in the thermal stabilization of PAN precursor fibres

著者 (7件)： Nunna Srinivas (Deakin University, Carbon Nexus, Institute for Frontier Materials, Geelong, Australia) ,  Creighton Claudia (Deakin University, Carbon Nexus, Institute for Frontier Materials, Geelong, Australia) ,  Hameed Nishar (Deakin University, Carbon Nexus, Institute for Frontier Materials, Geelong, Australia) ,  Naebe Minoo (Deakin University, Carbon Nexus, Institute for Frontier Materials, Geelong, Australia) ,  Henderson Luke C. (Deakin University, Carbon Nexus, Institute for Frontier Materials, Geelong, Australia) ,  Setty Mohan (Deakin University, Carbon Nexus, Institute for Frontier Materials, Geelong, Australia) ,  Fox Bronwyn L. (Factory of the Future, Swinburne University of Technology, Hawthorn, Australia)
資料名： Polymer Testing  (Polymer Testing)
巻： 59  ページ： 203-211  発行年： 2017年 
JST資料番号： C0752B  ISSN： 0142-9418  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ここでは,繊維構造の半径方向の不均一性と種々の温度で空気中および真空中における安定化したPAN繊維の性質の進化における酸素の役割について報告した。ナノインデンテーション法を用いた弾性率マッピングは空気中で処理したファイバにおける不均一な弾性率分布を示し,弾性率の変化は,真空中で処理した繊維では観察されなかった。Raman分光法と元素分析は,温度が皮膚空気処理試料のコアに比べて皮膚中のsp~II混成炭素の高い程度の進化における支援ファイバのコアへの酸素拡散に依存することを明らかにした。逆に,半径方向構造変化は真空処理した繊維では観察されなかった。空気処理した繊維の皮膚における高弾性率は高分子主鎖にC=C結合の形成により促進された拡張された分子間相互作用に関連した酸化的脱水素反応により促進されたコンパクトな構造の形成に起因した。これらの観察を支持して,SEMで調べ破壊形態はコアにおける皮膚と延性破壊における脆性破壊を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 元素分析 ,  高分子 ,  ナノインデンテーション ,  *前駆体 ,  不均一性 ,  弾性係数 ,  *熱安定化 ,  空気 ,  分子間相互作用 ,  Raman分光法 ,  *半径方向 ,  脆性破壊 ,  真空処理 ,  酸素 ,  酸化的脱水素

著者キーワード (6件)： 熱安定化 ,  酸化 ,  半径方向不均一性 ,  スキン-コア ,  ポリアクリロニトリル ,  炭素繊維

分類 (1件)： 充填剤,補強材  (YH05030J)

タイトルに関連する用語 (6件)： PAN ,  前駆体 ,  繊維 ,  熱安定化 ,  半径方向 ,  性質