化学ループ燃焼の還元過程における酸化鉄の焼結誘起された表面積崩壊の速度論【Powered by NICT】

Kinetics of sintering induced surface area decay of iron oxide in the reduction process of chemical looping combustion

著者 (3件)： Ma Zhong (Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education, School of Energy and Environment, Southeast University, Sipailou 2#, Nanjing, Jiangsu Province 210096, China) ,  Xiao Rui (Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education, School of Energy and Environment, Southeast University, Sipailou 2#, Nanjing, Jiangsu Province 210096, China) ,  Chen Liangyong (Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education, School of Energy and Environment, Southeast University, Sipailou 2#, Nanjing, Jiangsu Province 210096, China)
資料名： Fuel Processing Technology  (Fuel Processing Technology)
巻： 168  ページ： 20-26  発行年： 2017年 
JST資料番号： A0298B  ISSN： 0378-3820  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 化学ループ燃焼(CLC)は二酸化炭素(CO_2)を同時に分離できる高度な燃焼技術である。酸素担体のリサイクル性と安定性は,CLCの経済性にとって非常に重要である。酸素キャリアの不活性化のための主な因子は,焼結した。最もCLC研究のために,焦点は,酸素キャリアの反応性に及ぼす性であったが,酸素キャリアの焼結特性に寄与していた非常に少ない。CLCの還元過程における酸化鉄の表面積の特性と減衰の速度論を検討した。結果は反応温度を増加する酸化鉄の表面積の減少速度を加速することを示した。さらに,還元度深まりにつれて,酸化鉄の粒径は増加した。べき乗則表現モデルに基づく表面積崩壊の焼結速度を研究した。還元過程における表面積減少酸化鉄の活性化エネルギーは89.94kJ/molと計算された。焼結と酸素空格子点生成は還元プロセス中の酸化鉄のミクロ組織変化のための二原因であった。焼結は酸化鉄の表面積は減少したが,多孔質構造中の酸素空格子点生成の結果は,形成した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *酸化鉄 ,  活性化エネルギー ,  二酸化炭素 ,  粒径 ,  *焼結 ,  焼結性 ,  *表面積 ,  反応温度 ,  酸素 ,  *還元 ,  *速度論 ,  還元性
準シソーラス用語： 酸素空格子点 ,  酸素キャリア ,  *化学ループ燃焼 , 【Automatic Indexing@JST】

著者キーワード (5件)： 化学ループ燃焼 ,  酸化鉄 ,  焼結 ,  表面積崩壊 ,  酸素空格子点

分類 (1件)： 燃焼一般  (XE04010W)

タイトルに関連する用語 (9件)： 化学ループ燃焼 ,  還元 ,  過程 ,  酸化鉄 ,  焼結 ,  誘起 ,  表面積 ,  崩壊 ,  速度論