高熱伝導性・高強度Si_3N_4セラミックにおける酸化物と非酸化物添加物の比較研究【Powered by NICT】

Comparative study of oxide and non-oxide additives in high thermal conductive and high strength Si₃N₄ ceramics

著者 (4件)： Lee Hyun Min (Department of Materials Science and Engineering, Korea Advanced Institute of Science and Technology (KAIST), 291 Daehak-ro, Yuseong-gu, Daejeon, 34141 Republic of Korea) ,  Lee Eun Bok (Advanced Materials R&D Department, KCC Corporation, 19 Wanjusandan 4-ro, Wanju-gun, Jeonbuk-do, 55321 Republic of Korea) ,  Kim Dong Lae (Advanced Materials R&D Department, KCC Corporation, 19 Wanjusandan 4-ro, Wanju-gun, Jeonbuk-do, 55321 Republic of Korea) ,  Kim Do Kyung (Department of Materials Science and Engineering, Korea Advanced Institute of Science and Technology (KAIST), 291 Daehak-ro, Yuseong-gu, Daejeon, 34141 Republic of Korea)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 15  ページ： 17466-17471  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 酸化物と非酸化物焼結添加剤との間の比較研究は,Si_3N_4セラミックの熱的および機械的性質を調べるために行われた。微細構造,熱伝導率と機械的強度に及ぼす添加物タイプ(酸化物または非酸化物)の影響を調べた。非酸化物添加剤による酸化物添加剤の置換は焼結試料の第二相と格子酸素含有量の減少を誘導した。非酸化物焼結助剤の使用はSi_3N_4セラミックの熱伝導率を増加させた;が,焼結助剤はセラミック曲げ強さへの影響は少なかった。全ての試料の測定された強度は,822MPa~916MPaの範囲であった。,非酸化物焼結助剤を含むセラミックの熱伝導率は,増加した曲げ強さを維持しながらこれらの材料は862MPaの曲げ強さと熱伝導率101.5mKを有していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱伝導率 ,  焼結 ,  機械的強度 ,  *酸化物 ,  曲げ強さ ,  機械的性質 ,  *セラミック ,  第二相 ,  添加剤 ,  微細構造
準シソーラス用語： 焼結助剤 ,  酸素含有量 ,  *比較研究 ,  *高強度 ,  *熱伝導性 , 【Automatic Indexing@JST】

著者キーワード (5件)： Si_3N_4 ,  非酸化物添加剤 ,  熱伝導率 ,  曲げ強度 ,  Microstructure