Experimental study on mechanical properties and fracture toughness of thesimulated welded joint of big plate girder employed in boiler steel structure

著者 (4件)： Liao Xiaowei (Key Laboratory of Civil Engineering Safety and Durability of China Education Ministry, Department of Civil Engineering, Tsinghua University) ,  Wang Yuanqing (Key Laboratory of Civil Engineering Safety and Durability of China Education Ministry, Department of Civil Engineering, Tsinghua University) ,  Zhou Hui (Key Laboratory of Urban Security and Disaster Engineering of Ministry of Education, Beijing University of Technology) ,  Shi Yongjiu (Key Laboratory of Civil Engineering Safety and Durability of China Education Ministry, Department of Civil Engineering, Tsinghua University)
資料名： Tiedao Kexue Yugongcheng Xuebao  (Tiedao Kexue Yugongcheng Xuebao)
巻： 13  号： 9  ページ： 1803-1809  発行年： 2016年 
JST資料番号： C3009A  ISSN： 1672-7029  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ボイラの鋼構造物は,溶接と溶接において,亀裂欠陥を生じる。溶接継手の溶接性能を評価するために,破壊力学に基づく大板梁溶接欠陥の安全性評価のための基礎データを提供した。120MM厚さのQ345Bの下のフランジの溶接継手を,実際のシミュレーションによって構築し,そして,一軸引張,低温衝撃および三点曲げ破壊靱性試験を,行った。溶接継手の母材,熱影響部,および溶接継手の基本的機械的性質,衝撃靱性,および破壊靭性を研究した。研究結果は以下を示す。母材と熱影響部の鋼の機械的性質は安定しているが,溶接継手の機械的性質の指標は離散的である。温度の低下とともに,母材,熱影響部,および溶接部の衝撃力は減少した。溶接の延性-脆性転移温度は高く,CTODの固有値は小さく,靭性は劣っていた。厚板突合せ溶接継手の溶接部は溶接部の設計と評価の重点制御領域になる。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 溶接性 ,  *靱性 ,  *破壊靱性 ,  脆性 ,  衝撃 ,  破壊力学 ,  *溶接構造 ,  厚板 ,  *溶接 ,  転移温度 ,  溶接欠陥 ,  *溶接継手 ,  突合せ溶接継手 ,  *破壊靱性試験 ,  延性

著者キーワード (6件)： boiler steel structure ,  big plate girder ,  butt- welded joint ,  mechanical properties ,  impact toughness ,  fracture toughness