プラズマ火炎中のC/C ZrC SiC複合材料のミクロ構造及びアブレーション機構【Powered by NICT】

Microstructure and ablation mechanism of C/C-ZrC-SiC composites in a plasma flame

著者 (7件)： Wang Shaolei (Research Center of Composite Materials, Shanghai University, Shanghai 200072, China) ,  Li Hong (Research Center of Composite Materials, Shanghai University, Shanghai 200072, China) ,  Ren Musu (Research Center of Composite Materials, Shanghai University, Shanghai 200072, China) ,  Zuo Yazhuo (Research Center of Composite Materials, Shanghai University, Shanghai 200072, China) ,  Yang Min (Research Center of Composite Materials, Shanghai University, Shanghai 200072, China) ,  Zhang Jiabao (Research Center of Composite Materials, Shanghai University, Shanghai 200072, China) ,  Sun Jingliang (Research Center of Composite Materials, Shanghai University, Shanghai 200072, China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 14  ページ： 10661-10667  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： C/C-ZrC-SiC複合材料のアブレーション挙動をプラズマ火炎を用いて調べた。複合材料は優れた耐アブレーション性能を示した。180sのアブレーション後,表面中心に,温度と削剥力に密接に関連境界から出現した三種類のアブレーション挙動。さらに,複合材料の断面方向のアブレーション挙動は主に温度によって制御された。アブレーション中に,ZrCとSiCはZrO_2とSiO_2へ酸化され,それぞれ,ZrO_2~-SiO_2二成分共晶系を形成した。アブレーション機構も議論した,これは異なる温度で共晶系の進化過程の強い実例を提供することができた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *プラズマ ,  *アブレーション ,  *炭化ケイ素 ,  共晶 ,  *複合材料
準シソーラス用語： ミクロ構造 , 【Automatic Indexing@JST】

著者キーワード (3件)： C/C ZrC SiC複合材料 ,  Microstructure ,  アブレーション機構