流動沸騰におけるスマート表面ぬれ性の自発的変化【Powered by NICT】

Smart surface in flow boiling: Spontaneous change of wettability

著者 (7件)： Kim Jin Man (Division of Advanced Nuclear Engineering, POSTECH, Pohang 37673, Republic of Korea) ,  Kang Soon Ho (Korea Institute of Nuclear Safety, Daejeon 34142, Republic of Korea) ,  Yu Dong In (Division of Advanced Nuclear Engineering, POSTECH, Pohang 37673, Republic of Korea) ,  Park Hyun Sun (Division of Advanced Nuclear Engineering, POSTECH, Pohang 37673, Republic of Korea) ,  Moriyama Kiyofumi (Division of Advanced Nuclear Engineering, POSTECH, Pohang 37673, Republic of Korea) ,  Kim Moo Hwan (Division of Advanced Nuclear Engineering, POSTECH, Pohang 37673, Republic of Korea) ,  Kim Moo Hwan (Korea Institute of Nuclear Safety, Daejeon 34142, Republic of Korea)
資料名： International Journal of Heat and Mass Transfer  (International Journal of Heat and Mass Transfer)
巻： 105  ページ： 147-156  発行年： 2017年 
JST資料番号： C0390A  ISSN： 0017-9310  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,スマート表面として示唆された二酸化チタン(TiO_2)と酸化亜鉛(ZnO)被覆表面上での流動沸騰中の熱伝達係数(HTC)と臨界熱流束(CHF)を検討した。これら表面は最初に疎水性は早期発症核沸騰(ONB)を誘導し,多くの核形成サイトはSiO_2参照表面と比較して,沸騰の初期段階で観察された。その結果,高HTCは,スマート表面上で同定した。さらに,高い壁過熱条件の下で,表面は親水性になった乾燥地域への水供給を促進することによりCHFの分解ではなかった。結果は,スマート表面の濡れ性の自発的変化に起因した。熱処理を行った後,表面の接触角を調べた。温度が増加すると接触角は,スマート表面で減少した。結論として,著者らは,濡れ特性の変化はCHFを劣化させることなくHTCの改善を説明する上での重要な因子であり,スマート表面を示唆していると仮定した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 核形成 ,  酸化亜鉛 ,  給水 ,  疎水性 ,  過熱 ,  被覆 ,  熱処理 ,  核沸騰 ,  *濡れ ,  親水性 ,  熱伝達率 ,  接触角 ,  臨界熱流束
準シソーラス用語： 二酸化チタン ,  *流動沸騰 , 【Automatic Indexing@JST】

著者キーワード (6件)： 限界熱流束 ,  伝熱係数 ,  濡れ挙動 ,  TiO_2 ,  ZnO ,  流動沸騰