Geコアファイバの応力と構造特性に及ぼす焼なまし温度の影響【Powered by NICT】

Effect of annealing temperature on the stress and structural properties of Ge core fibre

著者 (5件)： Zhao Ziwen (Key Laboratory of Specialty Fiber Optics and Optical Access Networks, Shanghai University, Shanghai 200072, PR China) ,  Cheng Xueli (Key Laboratory of Specialty Fiber Optics and Optical Access Networks, Shanghai University, Shanghai 200072, PR China) ,  Xue Fei (Key Laboratory of Specialty Fiber Optics and Optical Access Networks, Shanghai University, Shanghai 200072, PR China) ,  He Ting (Key Laboratory of Specialty Fiber Optics and Optical Access Networks, Shanghai University, Shanghai 200072, PR China) ,  Wang Tingyun (Key Laboratory of Specialty Fiber Optics and Optical Access Networks, Shanghai University, Shanghai 200072, PR China)
資料名： Journal of Crystal Growth  (Journal of Crystal Growth)
巻： 473  ページ： 1-5  発行年： 2017年 
JST資料番号： B0942A  ISSN： 0022-0248  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 溶融炉心絞り(MCD)法によるGeコアファイバの応力と構造特性に及ぼすアニーリング温度の影響を,Raman分光法,走査電子顕微鏡(SEM),およびX線回折を用いて調べた。実験結果はGeファイバのRamanピーク位置は297.6cm~ 1から300.5cm~ 1にシフトし,FWHM値は4.53cm~ 1から4.31cm~ 1に減少し,アニーリングは700°C,800°C,900°Cで行い,それぞれであることが分かった。900°CでアニールしたGeコアでは,見かけの結晶粒をSEM画像で見られる,(331)面の回折ピークがX線回折スペクトルで生成した。これらの結果は,焼なまし温度を最適化Geコア中の残留応力の放出を可能にすることを示す。Geコアファイバは900°Cでアニールすると,それは最低残留応力と最高結晶品質を示し,800°Cでアニールした試料のそれに比べて品質改良は顕著であった。,約900°CでのアニーリングはGeコア繊維の品質を大きく改善できる。さらにアニーリング法によるGeコアファイバの性能向上が期待できる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶粒 ,  最適化 ,  *ゲルマニウム ,  *構造特性 ,  Raman分光法 ,  残留応力 ,  FWHM ,  走査電子顕微鏡 ,  *焼なまし ,  スペクトル ,  X線回折 ,  品質
準シソーラス用語： 結晶品質 ,  アニーリング温度 ,  *焼きなまし温度 , 【Automatic Indexing@JST】

著者キーワード (4件)： Geコアファイバ ,  アニーリング ,  残留応力 ,  結晶品質

分類 (1件)： 半導体薄膜  (BK14040E)

タイトルに関連する用語 (6件)： Ge ,  コア ,  ファイバ ,  応力 ,  構造特性 ,  焼なまし温度