αNaYF_4:NIRからNIRへの温度センシングのためのYb~3+ Tm~3+@CaF_2ナノ結晶【Powered by NICT】

α-NaYF₄:Yb³⁺-Tm³⁺@CaF₂ nanocrystals for NIR-to-NIR temperature sensing

著者 (7件)： Wu Ruozhen (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China) ,  Zhou Jiajia (College of Optical Science and Engineering, State Key Laboratory of Modern Optical Instrumentation, Zhejiang University, Hangzhou 310027, China) ,  Lei Lei (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China) ,  Zhang Shengjun (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China) ,  Xiao Zhen (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China) ,  Zhang Junjie (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China) ,  Xu Shiqing (College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018, China)
資料名： Chemical Physics Letters  (Chemical Physics Letters)
巻： 667  ページ： 206-210  発行年： 2017年 
JST資料番号： B0824A  ISSN： 0009-2614  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ドーピングアップコンバージョン温度センシングランタニドのアプローチはバイオサイエンスにおける高い優位性を示した。しかし,最もアップコンバージョンナノ温度計の生物学的透明窓(650 950nm)を超えた蛍光温度センシングを示した周辺環境の干渉を患っている。ここでは,NIR-to-NIR温度センシングを実現する敏感な性能を持つ,すなわちαNaYF_4:Yb Tm@CaF_2ナノ結晶,超小型サイズのナノプローブを報告した。Tm~3+イオンの3H_4→3H_6と1G_4→3H_6遷移による温度センシング感度を313-373Kの温度範囲で評価した。結果は,αNaYF_4:Yb Tm@CaF_2ナノ結晶は生物学的温度センシングのための有望な候補であることを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 周波数逓倍 ,  *ナノ結晶 ,  ライフサイエンス ,  温度計 ,  蛍光
準シソーラス用語： 温度範囲 ,  ナノプローブ ,  超小型 ,  *温度センシング , 【Automatic Indexing@JST】

著者キーワード (5件)： ランタニド ,  NIRからNIRへのアップコンバージョン ,  温度センシング ,  Stark副準位 ,  強度比

分類 (1件)： 無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (2件)： 温度センシング ,  ナノ結晶