高O_2~-ガス圧力下で作製した超高純度CrO_2の合成,構造及び磁気的性質【Powered by NICT】

Synthesis, structure and magnetic properties of ultra-high purity CrO₂ prepared under high O₂-gas pressure

著者 (6件)： Wang X.L. (Zhejiang Key Lab of Magnetic Materials, China Jiliang University, Hangzhou 310018, PR China) ,  Si P.Z. (Zhejiang Key Lab of Magnetic Materials, China Jiliang University, Hangzhou 310018, PR China) ,  Ge H.L. (Zhejiang Key Lab of Magnetic Materials, China Jiliang University, Hangzhou 310018, PR China) ,  Shinde K.P. (Powder & Ceramic Division, Korea Institute of Materials Science, Changwon, Gyeongnam 51508, Republic of Korea) ,  Chung K.C. (Powder & Ceramic Division, Korea Institute of Materials Science, Changwon, Gyeongnam 51508, Republic of Korea) ,  Choi C.J. (Powder & Ceramic Division, Korea Institute of Materials Science, Changwon, Gyeongnam 51508, Republic of Korea)
資料名： Solid State Sciences  (Solid State Sciences)
巻： 67  ページ： 72-75  発行年： 2017年 
JST資料番号： A0236B  ISSN： 1293-2558  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： フランス (FRA)  言語： 英語 (EN)

抄録/ポイント： 超高純度CrO_2はガス圧40MPaまでのO_2におけるCrO_3を分解することによって調製した,クロム酸化物の他の相の生成を防ぐためにCrO_3の分解過程を通して維持された。著者らの方法は,または周囲圧力下で始めることを従来の方法とは異なっている。高酸素圧は調製の初期段階からの安定な準安定CrO_2を可能にした。その結果,調製したままのCrO_2の純度が改善され,これはさらに試料の最高の磁化により証明した。調製されたままのCrO_2粒子は平坦な表面,八角形断面,直線エッジを持つ非常に大きな結晶粒を示し,融点以上の温度でCrO_2中のCrイオンの高い移動度に起因した。CrO_2の格子パラメータは4.4176Åと2.9144Åであった。高純度CrO_2粒子の磁気エントロピー変化の最大値は~1.5Tの印加磁場で2.83kg Kであった。純CrO_2の調製は,その固有特性を研究するためのおよびスピントロニクスデバイスへの応用のために重要である。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *クロム ,  酸化クロム ,  イオン ,  結晶粒 ,  *磁気的性質 ,  移動度 ,  融点 ,  格子定数 ,  *純度
準シソーラス用語： 印加磁場 ,  磁気エントロピー変化 ,  酸素分圧 ,  *ガス圧 ,  *高純度 , 【Automatic Indexing@JST】

著者キーワード (3件)： 高純度CrO_2 ,  高酸素圧 ,  磁気的性質

分類 (1件)： 金属酸化物及び金属カルコゲン化物の結晶構造  (BK07020Y)

タイトルに関連する用語 (4件)： ガス圧力 ,  作製 ,  高純度 ,  磁気的性質