(6,5)より薄い単層カーボンナノチューブの効率的成長のための拡張アルコール触媒化学蒸着【Powered by NICT】

Extended alcohol catalytic chemical vapor deposition for efficient growth of single-walled carbon nanotubes thinner than (6,5)

著者 (7件)： Hou Bo (Energy NanoEngineering Lab., Department of Energy and Environment, AIST, Tsukuba 305-8564, Japan) ,  Wu Cheng (Department of Mechanical Engineering, The University of Tokyo, Tokyo 113-8656, Japan) ,  Inoue Taiki (Department of Mechanical Engineering, The University of Tokyo, Tokyo 113-8656, Japan) ,  Chiashi Shohei (Department of Mechanical Engineering, The University of Tokyo, Tokyo 113-8656, Japan) ,  Xiang Rong (Department of Mechanical Engineering, The University of Tokyo, Tokyo 113-8656, Japan) ,  Maruyama Shigeo (Energy NanoEngineering Lab., Department of Energy and Environment, AIST, Tsukuba 305-8564, Japan) ,  Maruyama Shigeo (Department of Mechanical Engineering, The University of Tokyo, Tokyo 113-8656, Japan)
資料名： Carbon  (Carbon)
巻： 119  ページ： 502-510  発行年： 2017年 
JST資料番号： H0270B  ISSN： 0008-6223  CODEN： CRBNA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： アルコール触媒化学蒸着(ACCVD)合成単層カーボンナノチューブ(SWCNTs)の包括的な調査を行い,70以上の温度-圧力セットを用いて,340から950°Cまでの広い温度範囲と大きさの6桁以上の広い圧力範囲をカバーする拡張ACCVDパラメトリックマップを示した。高品質SWCNTsの効率的な合成を,温度400 °C,圧力10~ 2Pa,この探査に新たに発見された温度と圧力の間の強い相関から利益を得るまでで可能になる。基になる機構は,速度論的モデルを用いて明らかにし,拡張実験地図上二増殖境界は輸送のない透過型電子顕微鏡(TEM)観察により説明した。最も重要なことは,ACCVDの成長窓を拡張した後,極端に低い温度と圧力での合成の成功は,直接合成から観察されることが少ないことのより薄い超直径のSWCNTs(0.8nm>d>0.62nm)で有意に増強された収率(6, 5)を与えた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *単層カーボンナノチューブ ,  *アルコール ,  速度論 ,  透過型電子顕微鏡
準シソーラス用語： *触媒化学 ,  直接合成 ,  高品質 ,  温度範囲 ,  *Cat-CVD , 【Automatic Indexing@JST】

著者キーワード (4件)： 単層カーボンナノチューブ ,  アルコール触媒化学気相蒸着 ,  小口径 ,  成長機構

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (5件)： 単層カーボンナノチューブ ,  成長 ,  拡張 ,  アルコール ,  触媒化学蒸着