リチウムイオン電池用のカソード材料としての調製とグラフェン表面被覆NaTi_2(PO_4)_3【Powered by NICT】

The preparation and graphene surface coating NaTi₂(PO₄)₃ as cathode material for lithium ion batteries

著者 (6件)： Li Na (Department of Chemical and Chemical Engineering, Hefei normal University, Hefei, Anhui 230601, China) ,  Wang Yanping (Department of Chemical and Chemical Engineering, Hefei normal University, Hefei, Anhui 230601, China) ,  Rao Richuan (Department of Chemical and Chemical Engineering, Hefei normal University, Hefei, Anhui 230601, China) ,  Dong Xiongzi (Department of Chemical and Chemical Engineering, Hefei normal University, Hefei, Anhui 230601, China) ,  Zhang Xianwen (Institute of Advanced Energy Technology & Equipment, Hefei University of Technology, 193 Tunxi Road, Hefei, Anhui 230009, China) ,  Zhu Sane (Department of Chemistry and Materials Engineering, Hefei University, Hefei, Anhui 230601, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 399  ページ： 624-629  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： グラフェン被覆NaTi_2(PO_4)3を簡単なゾル-ゲルプロセスとそれに続く焼成により作製した。NaTi_2(PO_4)グラフェン(NTP/G)複合材料を,リチウムイオン電池のカソード電極材料として直接使用し,この系における複合材料の電気化学的特性を,最初に詳細に研究した。充放電プロセスでは,ほとんどすべてのNa~+であるフレームワークを維持する固定化二Li~+は八面体M(2)サイトを占有し,イオン伝導チャネルを通るNTPの3D骨格に可逆的にインターカレーションすることができた。5Cレートで,800サイクル後NTP/G複合材料の容量保持は82.7%であった。NTP/Gの優れた電気化学的特性はその安定な三次元フレームワークと強化された電子伝導に起因するグラフェンシート表面改質に起因している。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： イオン伝導 ,  複合材料 ,  表面改質 ,  *グラフェン ,  三次元 ,  電極材料 ,  ゲル ,  八面体 ,  *表面被覆 ,  インターカレーション ,  *リチウムイオン電池
準シソーラス用語： 電子伝導 ,  充放電 ,  電気化学的特性 ,  *正極材料 , 【Automatic Indexing@JST】

著者キーワード (5件)： NaTi_2(PO_4)_3/graphene複合材料 ,  ゾル-ゲル合成 ,  表面改質 ,  リチウムイオン電池 ,  電気化学的性質

分類 (2件)： 二次電池  (YB04030K) ,  電極過程  (CB07040U)

タイトルに関連する用語 (5件)： リチウムイオン電池 ,  カソード材料 ,  調製 ,  グラフェン ,  表面被覆