ZnOナノ粒子導入されたMg-Y合金におけるss_1′Mg-Znリッチ相のその場発生による強化【Powered by NICT】

Strengthening due to the in-situ evolution of ss₁′ Mg-Zn rich phase in a ZnO nanoparticles introduced Mg-Y alloy

著者 (5件)： Tekumalla S. (Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, Singapore 117576, Singapore) ,  Shabadi R. (Laboratory of Physical Metallurgy and Materials Engineering, Unite Materiaux Et Transformations, UMR CNRS 8207, Universite Lille - 1 Sciences et Technologies, 59650-Villeneuve d’Ascq, France) ,  Yang Chen (Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, Singapore 117576, Singapore) ,  Seetharaman S. (Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, Singapore 117576, Singapore) ,  Gupta M. (Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, Singapore 117576, Singapore)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 133  ページ： 29-32  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Mg-Y合金へのZnOナノ粒子の添加は,マトリックスにおけるYからイットリアナノ粒子のナノスケールのMg-Znリッチss_1’相と形成のその場発生を導くZnOの減少をもたらすことを,透過型電子顕微鏡及び示差走査熱量測定によって特性化した。モノリシックMg-1.8Y合金と比較してss_1’相(強化相)の結晶粒微細化と進化は,Mg-1.8Y/1In0.53ZnOナノ複合材料の降伏強さの著しい改善をもたらした。,従来法に比べて,この方法は優れた特性を有するマグネシウムマトリックスナノ複合材料のその場製造に用いることができる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ナノ複合材料 ,  *ナノ粒子 ,  示差走査熱量測定 ,  降伏強さ ,  キャラクタリゼーション ,  *合金 ,  *酸化亜鉛 ,  結晶粒微細化 ,  酸化イットリウム ,  透過型電子顕微鏡
準シソーラス用語： ナノスケール ,  *酸化亜鉛ナノ粒子 , 【Automatic Indexing@JST】

著者キーワード (5件)： マグネシウム ,  Nanoparticles ,  その場進化 ,  ナノss_1’相 ,  降伏強さ

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： ZnOナノ粒子 ,  Mg ,  Y合金 ,  Zn ,  強化