ナノサイズZrB_2粉末を用いた単一ステップと最適化された2段階ホットプレスによるZrB_2SiCセラミックの調製【Powered by NICT】

Preparation of ZrB₂-SiC ceramics by single-step and optimized two-step hot pressing using nanosized ZrB₂ powders

著者 (4件)： Hu Ping (National Key Laboratory of Science and Technology on Advanced Composites in Special Environments, Harbin Institute of Technology, Harbin 150001, PR China) ,  Gui Kaixuan (National Key Laboratory of Science and Technology on Advanced Composites in Special Environments, Harbin Institute of Technology, Harbin 150001, PR China) ,  Hong Wenhu (National Key Laboratory of Science and Technology on Advanced Composites in Special Environments, Harbin Institute of Technology, Harbin 150001, PR China) ,  Zhang Xinghong (National Key Laboratory of Science and Technology on Advanced Composites in Special Environments, Harbin Institute of Technology, Harbin 150001, PR China)
資料名： Materials Letters  (Materials Letters)
巻： 200  ページ： 14-17  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ZrB_2SiCセラミックスはナノサイズZrB_2粉末を用いた1500~1800°Cの温度範囲で一段階ホットプレスにより調製した。高曲げ強さ(1044±79MPa)および破壊靭性(6.21±0.25MPa m~1/2)を用いた高密度ZrB_2SiCは1800°Cで得られた。最適化した二段階ホットプレスプロセスを設計し,低温で高い相対密度(>98%)ZrB_2SiCセラミックの製造における大きな利点を示した。さらに,高い曲げ強さ(901±65MPa)が得られ,同じ焼結温度で一段階ホットプレスによるZrB_2SiC(587±72MPa)のそれよりもはるかに高かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *セラミック ,  *粉体 ,  低温 ,  *最適化 ,  曲げ強さ ,  相対密度 ,  *ホットプレス ,  破壊靱性
準シソーラス用語： 焼結温度 ,  高密度 ,  温度範囲 , 【Automatic Indexing@JST】

著者キーワード (5件)： セラミックス ,  ZrB_2 ,  ナノサイズ ,  ホットプレス ,  曲げ強度

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (7件)： ナノサイズ ,  粉末 ,  最適化 ,  段階 ,  ホットプレス ,  セラミック ,  調製