SnO_2/SiO_2コーティングとポリイミド膜とその応用原子状酸素防護の間の接着性の改善【Powered by NICT】

Improved adhesion between SnO₂/SiO₂ coating and polyimide film and its applications to atomic oxygen protection

著者 (5件)： Liu Kai (College of Chemistry and Chemical Engineering, Yantai University, Yantai 264005, PR China) ,  Mu Huifeng (College of Chemistry and Chemical Engineering, Yantai University, Yantai 264005, PR China) ,  Shu Ming (College of Chemistry and Chemical Engineering, Yantai University, Yantai 264005, PR China) ,  Li Zhonghua (National Key Lab. of Science and Technology on Vacuum Technology & Physics, Lanzhou Institute of Physics, Lanzhou 730000, PR China) ,  Gao Yuan (College of Chemistry and Chemical Engineering, Yantai University, Yantai 264005, PR China)
資料名： Colloids and Surfaces. A. Physicochemical and Engineering Aspects  (Colloids and Surfaces. A. Physicochemical and Engineering Aspects)
巻： 529  ページ： 356-362  発行年： 2017年 
JST資料番号： A0539B  ISSN： 0927-7757  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： シリカカップリング剤と組み合わせたアルカリ溶液は,無機被覆とポリイミド基板の間の接着を改善するためのポリイミドの表面を改質するために使用した。NaOHとγ-アミノプロピルトリエトキシシラン(APTES)による表面処理後,ポリイミド基板の水接触角は大きく減少してSnO_2/SiO_2被覆をゾル-ゲル法によりそれに容易に形成した。被覆層の数は3層から7層に増加するとSnO_2/SiO_2被覆試料の光透過率は安定していた。SnO_2/SiO_2被覆の原子状酸素(AO)抵抗は耐久性評価のための地上ベースのAOシミュレーションシステムで行った。AO照射の前後で,表面の形態変化を走査電子顕微鏡(SEM)により解析した。結果は,この方法で調製した被覆は基材をAO浸食に非常に高品質保護を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 被覆層 ,  走査電子顕微鏡 ,  *被覆 ,  二酸化ケイ素 ,  浸食 ,  *ポリイミド ,  耐久試験 ,  カップリング剤 ,  ゾル-ゲル法
準シソーラス用語： 高品質 ,  光透過率 ,  水接触角 ,  アルカリ溶液 ,  *粘着性 ,  *原子状酸素 , 【Automatic Indexing@JST】

著者キーワード (5件)： SnO_2/SiO_2コーティング ,  ポリイミド ,  表面改質 ,  アルカリ解 ,  酸素原子

分類 (2件)： 固-固界面  (CB12060M) ,  コロイド化学一般  (CB11010C)

タイトルに関連する用語 (6件)： コーティング ,  ポリイミド膜 ,  応用 ,  原子状酸素 ,  防護 ,  接着性