8mol%(SmO1.5,GdO1.5,およびYO1.5)安定化ZrO2粉末の相変態と結晶成長挙動【JST・京大機械翻訳】

著者 (5件)： R.Mahendran (DEPARTMENT OF METALLURGICAL AND MATERIALS ENGINEERING, NATIONAL INSTITUTE OF TECHNOLOGY, TIRCHIRAPPALLI 620015, TAMIL NADU, INDIA) ,  S.P. Kumaresh Babu (DEPARTMENT OF METALLURGICAL AND MATERIALS ENGINEERING, NATIONAL INSTITUTE OF TECHNOLOGY, TIRCHIRAPPALLI 620015, TAMIL NADU, INDIA) ,  S. Natarajan (DEPARTMENT OF METALLURGICAL AND MATERIALS ENGINEERING, NATIONAL INSTITUTE OF TECHNOLOGY, TIRCHIRAPPALLI 620015, TAMIL NADU, INDIA) ,  S. Manivannan (DEPARTMENT OF METALLURGICAL AND MATERIALS ENGINEERING, NATIONAL INSTITUTE OF TECHNOLOGY, TIRCHIRAPPALLI 620015, TAMIL NADU, INDIA) ,  A. Vallimanalan (DEPARTMENT OF METALLURGICAL AND MATERIALS ENGINEERING, NATIONAL INSTITUTE OF TECHNOLOGY, TIRCHIRAPPALLI 620015, TAMIL NADU, INDIA)
資料名： International Journal of Minerals, Metallurgy and Materials  (International Journal of Minerals, Metallurgy and Materials)
巻： 24  号： 7  ページ： 842-849  発行年： 2017年 
JST資料番号： W1051A  ISSN： 1674-4799  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： ZrO2-8mol% SmO1.5(8SmSZ),ZrO2-8mol%GdO1.5(8GdSZ),ZrO2-8mol%YO1.5(8YSZ)のナノ結晶粉末を簡単な逆共沈法により作製した。示差熱分析/熱重量分析(DTA/TG),Fourier変換赤外分光法(FTIR),X線回折(XRD),Raman分光法,および高分解能透過型電子顕微鏡(HRTEM)を用いて,相変態と結晶成長挙動を研究した。DTAの結果は,ZrO2の凍結乾燥析出物が,8SmSZ,8GdSZ,8YSZの場合に,それぞれ529,465,および467°Cで結晶化することを示した。XRDとRamanの結果は,乾燥した析出物が600~1000°Cの温度範囲で2時間焼成されたとき,正方晶ZrO2の存在を確認した。結晶サイズは焼成温度の上昇と共に増加した。活性化エネルギーは,8SmSZ,8GdSZおよび8YSZに対してそれぞれ12.39,12.45および16.59kJ/molと計算された。Data from Wanfang. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *粉体 ,  正方晶系 ,  *酸化ジルコニウム ,  Raman分光法 ,  結晶化 ,  *結晶成長 ,  X線回折 ,  熱重量分析 ,  共沈 ,  示差熱分析 ,  ナノ結晶 ,  析出物 ,  活性化エネルギー
準シソーラス用語： 焼成温度 ,  HRTEM , 【Automatic Indexing@JST】

分類 (3件)： セラミック・陶磁器の製造  (YC03020V) ,  炭素とその化合物  (YB02060D) ,  原子・分子のクラスタ  (BH09030O)

タイトルに関連する用語 (6件)： 安定化 ,  ZrO2 ,  粉末 ,  相変態 ,  結晶成長 ,  挙動