CoをドープしたLaMnO_3ナノ構造におけるGriffiths相の低温核形成【Powered by NICT】

Low temperature nucleation of Griffiths Phase in Co doped LaMnO₃ nanostructures

著者 (7件)： Adeela N. (Division of Energy and Environment, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China) ,  Adeela N. (Centre for High Energy Physics, University of the Punjab, Lahore 54000, Pakistan) ,  Khan U. (Centre for High Energy Physics, University of the Punjab, Lahore 54000, Pakistan) ,  Naz S. (Department of Mathematics, University of Gujrat, Gujrat 54700, Pakistan) ,  Iqbal M. (Centre for High Energy Physics, University of the Punjab, Lahore 54000, Pakistan) ,  Irfan M. (Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China) ,  Cheng Y. (Division of Energy and Environment, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 422  ページ： 184-191  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 水熱法で合成したLa_1Co_x MnO_3ナノ構造の磁気特性を報告した。結晶構造をX線回折(XRD)法によって特性化したが,これは室温で菱面体晶ペロブスカイト構造を示した。走査電子顕微鏡(SEM)およびエネルギー分散X線分光法(EDS)は,調製したナノ粒子の形態と化学組成を分析するために使用されてきた。全試料の磁気ヒステリシスループは,10Kで強磁性挙動を示した。温度の関数としての逆感受性グラフはCurie-Weiss則からのずれを表している。Curie温度よりも十分に短距離強磁性クラスタの適応はGriffiths相(GP)に起因して観察された。GPの存在は,LaとCoイオンの誘起サイズ効果から生じることを提案した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： Curie-Weiss則 ,  エネルギー分散X線分光分析 ,  強磁性 ,  三方晶系 ,  Curie温度 ,  結晶構造 ,  *ドーピング ,  サイズ効果 ,  化学組成 ,  *ナノ構造 ,  水熱合成 ,  *ランタン ,  磁気ヒステリシス
準シソーラス用語： ペロブスカイト型構造 ,  *Griffiths相 , 【Automatic Indexing@JST】

著者キーワード (4件)： ペロブスカイト構造 ,  Curie Weiss則 ,  Griffiths相 ,  水熱法