酸素発生反応の効率的な電極触媒用の窒素ドープカーボンナノチューブに埋め込まれた配位重合体誘導されたコバルト【Powered by NICT】

Coordination polymer derived cobalt embedded in nitrogen-doped carbon nanotubes for efficient electrocatalysis of oxygen evolution reaction

著者 (12件)： Cong Jingkun (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Li Changqing (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Zhao Tao (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Wu Jin (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Zhang Rui (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Ren Wenjing (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Wang Shunli (Department of Physics, Center for Optoelectronic Materials and Devices, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Gao Junkuo (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Gao Junkuo (State Key Laboratory of Silicon Materials, College of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, PR China) ,  Liu Yi (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Liu Yi (State Key Laboratory of Silicon Materials, College of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, PR China) ,  Yao Juming (The Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, National Engineering Lab for Textile Fiber Materials and Processing Technology (Zhejiang), College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, PR China)
資料名： Journal of Solid State Chemistry  (Journal of Solid State Chemistry)
巻： 253  ページ： 227-230  発行年： 2017年 
JST資料番号： H0505A  ISSN： 0022-4596  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本論文では,前駆体としてCoメラミン配位重合体(CP)を用いてCo埋め込み窒素ドープカーボンナノチューブ(Co NCNT)の作製を報告した。試料は,SEM,TEM,XRD,XPSおよびBET法によって特性化した。Co NCNTは,OERのための優れた安定な触媒性能を示した。10mAcm~ 2でCo NCNTの過電圧は370mV(vs RHE)である。Co NCNTの電流密度は,520mVの過電圧,RuO_2よりもはるかに良好な性能を示した,100macm~ 2に達し,一方RuO_2の最大電流密度は44macm~ 2だけで達することができた。Co NCNTのTafel勾配は56mVdec~ 1であり,市販RuO_2(58mVdec~ 1)のそれよりも小さかった。結果は金属メラミンベースCPまたはMOFは,電極触媒反応のための効率的な金属埋め込み窒素ドープ炭素材料の調製のための有望な前駆体であることを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *カーボンナノチューブ ,  前駆体 ,  触媒活性 ,  炭素材 ,  X線回折 ,  過電圧 ,  *配位高分子 ,  BET法 ,  *電極触媒 ,  電流密度 ,  *コバルト ,  キャラクタリゼーション
準シソーラス用語： 電気触媒反応 ,  *窒素ドーピング ,  *酸素発生反応 , 【Automatic Indexing@JST】

著者キーワード (5件)： 配位重合体 ,  カーボンナノチューブ ,  酸素発生反応 ,  Overpotential ,  電極触媒作用

分類 (2件)： 塩基,金属酸化物  (CD01030Z) ,  金属酸化物及び金属カルコゲン化物の結晶構造  (BK07020Y)

タイトルに関連する用語 (7件)： 酸素発生反応 ,  電極触媒 ,  窒素ドープ ,  カーボンナノチューブ ,  配位重合体 ,  誘導 ,  コバルト